| - The coatings were deposited in a multi magnetron Teer sputtering device with two C targets and a Ti target in Ar atmosphere, on steel and Si substrates. To deposit hydrogenated coatings methane was introduced in the discharge atmosphere. The films were deposited in a range of 7e14 at.% Ti content. X-ray diffraction patterns revealed the presence of a nanocrystalline TiC phase. The hardness varied from 8 to 9 GPa. The tribological tests were performed under dry sliding and lubricated (0.9% NaCl water solution, physiological solution, PS, and 10% fetal bovine serum dissolved in Ringer's saline solution, FBS) conditions, using a 100Cr6 steel balls with a diameter of 6 mm, in a pin-on-disc wear test apparatus.
- The coatings were deposited in a multi magnetron Teer sputtering device with two C targets and a Ti target in Ar atmosphere, on steel and Si substrates. To deposit hydrogenated coatings methane was introduced in the discharge atmosphere. The films were deposited in a range of 7e14 at.% Ti content. X-ray diffraction patterns revealed the presence of a nanocrystalline TiC phase. The hardness varied from 8 to 9 GPa. The tribological tests were performed under dry sliding and lubricated (0.9% NaCl water solution, physiological solution, PS, and 10% fetal bovine serum dissolved in Ringer's saline solution, FBS) conditions, using a 100Cr6 steel balls with a diameter of 6 mm, in a pin-on-disc wear test apparatus. (en)
|
Title
| - Tribological behaviour a-C and a-C:H films doped with Ti in biological solutions
- Tribological behaviour a-C and a-C:H films doped with Ti in biological solutions (en)
|
skos:prefLabel
| - Tribological behaviour a-C and a-C:H films doped with Ti in biological solutions
- Tribological behaviour a-C and a-C:H films doped with Ti in biological solutions (en)
|
skos:notation
| - RIV/68407700:21230/11:00180835!RIV12-GA0-21230___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/68407700:21230/11:00180835
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - a-C and a-C:H coatings, Ti doping, Tribology effects, Biological lubricants (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| - GB - Spojené království Velké Británie a Severního Irska
|
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Cavaleiro, A.
- Escudeiro, A.
- Polcar, Tomáš
|
http://linked.open...ain/vavai/riv/wos
| |
issn
| |
number of pages
| |
http://bibframe.org/vocab/doi
| - 10.1016/j.vacuum.2011.03.011
|
http://localhost/t...ganizacniJednotka
| |