| - The report deals with the issue of laser beam interaction with the surface Al-alloy used in aircraft industry. Laser beam was generated by two different laser generators. Firstly was used pulse generator Nd:YAG laser with wavelength 1060 nm, frequency range 1 - 18 kHz and the peak output 50 W. The feed speed of the laser beam was chosen from 5 to the 35 mm.s-1. Secondly was used continual laser beam generated by diode laser with the output 3.1 kW. The material, which was used for the experiments, was a commercial EN AW - 2024 - T3 (4,4% Cu, 1,5% Mg, 0,6% Mn, solution treated, cold rolled and naturally aged) in plate form with a thickness 0.8 mm.
- The report deals with the issue of laser beam interaction with the surface Al-alloy used in aircraft industry. Laser beam was generated by two different laser generators. Firstly was used pulse generator Nd:YAG laser with wavelength 1060 nm, frequency range 1 - 18 kHz and the peak output 50 W. The feed speed of the laser beam was chosen from 5 to the 35 mm.s-1. Secondly was used continual laser beam generated by diode laser with the output 3.1 kW. The material, which was used for the experiments, was a commercial EN AW - 2024 - T3 (4,4% Cu, 1,5% Mg, 0,6% Mn, solution treated, cold rolled and naturally aged) in plate form with a thickness 0.8 mm. (en)
- Příspěvek se zabývá výsledkem interakce laserového paprsku s povrchem hliníkové slitiny používané pro letecké aplikace. Laserové záření bylo generováno dvěma laserovými zdroji. Jednak byl použit pulzní generátor Nd:YAG laser (s vlnovou délkou 1060 nm, s frekvencí 1 - 18 kHz a výstupním špičkovým výkonem 50 W; rychlost posuvu pulzního paprsku byla volena od 5 do 35 mm.s-1) a jednak kontinuální laserový paprsek generovaný diodovým laserem s výstupním výkonem až 3,1 kW. Materiálem určeným pro experimenty byla slitina hliníku EN AW- 2024 ve stavu T3 (žíháno na rozpouštěcí teplotu, zpracováno za studena a přirozeně stárnuto) ve formě plechu o tloušťce 0,8 mm. (cs)
|
Title
| - Laser Surface Treatment of 2024 - T3 Aluminium Alloy
- Laser Surface Treatment of 2024 - T3 Aluminium Alloy (en)
- Přepracování povrchu hliníkové slitiny 2024 - T3. (cs)
|
skos:prefLabel
| - Laser Surface Treatment of 2024 - T3 Aluminium Alloy
- Laser Surface Treatment of 2024 - T3 Aluminium Alloy (en)
- Přepracování povrchu hliníkové slitiny 2024 - T3. (cs)
|
skos:notation
| - RIV/68407700:21220/07:02141068!RIV08-MSM-21220___
|
http://linked.open.../vavai/riv/strany
| |
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/68407700:21220/07:02141068
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - Aluminium alloy; Laser treatment; Surface (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| - Proceedings of Workshop 2007
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Cejp, Jiří
- Pavlásková, I.
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
http://linked.open...n/vavai/riv/zamer
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| - České vysoké učení technické v Praze
|
https://schema.org/isbn
| |
http://localhost/t...ganizacniJednotka
| |