| - Crystal (Lu0.1Y0.9)AlO3:Nd0.1% was grown by the u-PD method and annealed for 20 hours in oxygen atmosphere. The XRD results for all the samples were consistent with JCPDS data (#33-0041), a space group of orthorhombic Pbnm while no impurity peaks were observed. Intense absorption peaks were observed approximately at 240 and 290 nm ascribed tp the two-electron F center and one-electron F+ center, respectively. These absorptions were enhanced by Lu substitution. The radio-luminescence spectra show several emission peaks due to Nd3+ 4f-4f transitions and the most intense of which were assigned to 2F(2)5/2-4F5/2, 2F(2)5/2-4G7/2 and 2F(2)5/2-4G9/2 transitions at 395, 540 and 550 nm, respectively. The light yield after annealing annealing was as high as 5025 +-500 (Nphe/MeV) when using Si-APD (S8664). The scintillation decay time constants were evaluated to be 3.44–3.80 us for each sample.
- Crystal (Lu0.1Y0.9)AlO3:Nd0.1% was grown by the u-PD method and annealed for 20 hours in oxygen atmosphere. The XRD results for all the samples were consistent with JCPDS data (#33-0041), a space group of orthorhombic Pbnm while no impurity peaks were observed. Intense absorption peaks were observed approximately at 240 and 290 nm ascribed tp the two-electron F center and one-electron F+ center, respectively. These absorptions were enhanced by Lu substitution. The radio-luminescence spectra show several emission peaks due to Nd3+ 4f-4f transitions and the most intense of which were assigned to 2F(2)5/2-4F5/2, 2F(2)5/2-4G7/2 and 2F(2)5/2-4G9/2 transitions at 395, 540 and 550 nm, respectively. The light yield after annealing annealing was as high as 5025 +-500 (Nphe/MeV) when using Si-APD (S8664). The scintillation decay time constants were evaluated to be 3.44–3.80 us for each sample. (en)
|
Title
| - Investigations of optical and scintillation properties of (Lu0.1Y0.9)AlO3:Nd0.1%
- Investigations of optical and scintillation properties of (Lu0.1Y0.9)AlO3:Nd0.1% (en)
|
skos:prefLabel
| - Investigations of optical and scintillation properties of (Lu0.1Y0.9)AlO3:Nd0.1%
- Investigations of optical and scintillation properties of (Lu0.1Y0.9)AlO3:Nd0.1% (en)
|
skos:notation
| - RIV/68378271:_____/12:00385506!RIV13-AV0-68378271
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/68378271:_____/12:00385506
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - crystals; lutetium; x-ray detectors (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| - US - Spojené státy americké
|
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| - IEEE Transactions on Nuclear Science
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Fujimoto, Y.
- Pejchal, Jan
- Sugiyama, M.
- Totsuka, D.
- Yanagida, T.
- Yokota, Y.
- Yoshikawa, A.
|
http://linked.open...ain/vavai/riv/wos
| |
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://bibframe.org/vocab/doi
| |