| - Development of optomechanical composites’, based on glass matrices reinforced with continuous oxide fibre bundles (Nextel) or filaments (sapphire) is described. The fibres were arranged unidirectionally between soda-lime silicate or borosilicate glass slides, and heat-treated to achieve densification by viscous flow of the glass matrix between the fibres. Small decreases in light transmittance (up to approximately 20%) upon introduction of fibres was indicated. Fibre pull-out and crack deflection were identified at fibre/matrix interfaces, and a crack bridging effect was observed, with fibres holding the glass pieces together, thus preventing catastrophic failure. A relatively low fibre/matrix interfacial sliding resistance was measured by the fibre push-in test, although flexural strength measurements indicated the need to improve interfacial bonding.
- Development of optomechanical composites’, based on glass matrices reinforced with continuous oxide fibre bundles (Nextel) or filaments (sapphire) is described. The fibres were arranged unidirectionally between soda-lime silicate or borosilicate glass slides, and heat-treated to achieve densification by viscous flow of the glass matrix between the fibres. Small decreases in light transmittance (up to approximately 20%) upon introduction of fibres was indicated. Fibre pull-out and crack deflection were identified at fibre/matrix interfaces, and a crack bridging effect was observed, with fibres holding the glass pieces together, thus preventing catastrophic failure. A relatively low fibre/matrix interfacial sliding resistance was measured by the fibre push-in test, although flexural strength measurements indicated the need to improve interfacial bonding. (en)
|
Title
| - Optically-transparent oxide fibre-reinforced glass matrix composites
- Optically-transparent oxide fibre-reinforced glass matrix composites (en)
|
skos:prefLabel
| - Optically-transparent oxide fibre-reinforced glass matrix composites
- Optically-transparent oxide fibre-reinforced glass matrix composites (en)
|
skos:notation
| - RIV/68081723:_____/10:00355562!RIV11-GA0-68081723
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(GA101/09/1821), Z(AV0Z20410507)
|
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/68081723:_____/10:00355562
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - fracture toughness; glas matrix composites; light transmittance (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| - Journal of Non-Crystalline Solids
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Boccaccini, A. R.
- Dlouhý, Ivo
- Desimone, D.
- Horvath, J.
- Koch, D.
- Lee, W. E.
|
http://linked.open...ain/vavai/riv/wos
| |
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |