About: Modelling of damage accumulation under cyclic loading. Study of nucleation and propagation of fatigue cracks. Comparison of physically short cracks against macroscopic cracks under cyclic fatigue     Goto   Sponge   NotDistinct   Permalink

An Entity of Type : http://linked.opendata.cz/ontology/domain/vavai/Vysledek, within Data Space : linked.opendata.cz associated with source document(s)

AttributesValues
rdf:type
Description
  • Bylo studováno chování feriticko-martensitické oceli Eurofer s omezenou aktivací během cyklického zatěžování. Byla nalezena typická místa nukleace trhlin a byly změřeny parametry šíření mikrostrukturně krátkých i dlouhých trhlin. (cs)
  • Behavior of reduced activation martensitic ferritic Eurofer steel under cyclic loading was studied. Crack nucleation sites were detected and propagation of microstructuraly short and long cracks was measured.
  • Behavior of reduced activation martensitic ferritic Eurofer steel under cyclic loading was studied. Crack nucleation sites were detected and propagation of microstructuraly short and long cracks was measured. (en)
Title
  • Modelling of damage accumulation under cyclic loading. Study of nucleation and propagation of fatigue cracks. Comparison of physically short cracks against macroscopic cracks under cyclic fatigue
  • Modelování poškození při cyklickém zatěžování. Studium nukleace a šíření únavových trhlin. Srovnání mikrostrukturně krátkých a dlouhých trhlin (cs)
  • Modelling of damage accumulation under cyclic loading. Study of nucleation and propagation of fatigue cracks. Comparison of physically short cracks against macroscopic cracks under cyclic fatigue (en)
skos:prefLabel
  • Modelling of damage accumulation under cyclic loading. Study of nucleation and propagation of fatigue cracks. Comparison of physically short cracks against macroscopic cracks under cyclic fatigue
  • Modelování poškození při cyklickém zatěžování. Studium nukleace a šíření únavových trhlin. Srovnání mikrostrukturně krátkých a dlouhých trhlin (cs)
  • Modelling of damage accumulation under cyclic loading. Study of nucleation and propagation of fatigue cracks. Comparison of physically short cracks against macroscopic cracks under cyclic fatigue (en)
skos:notation
  • RIV/68081723:_____/07:00094702!RIV08-AV0-68081723
http://linked.open...avai/riv/aktivita
http://linked.open...avai/riv/aktivity
  • Z(AV0Z20410507)
http://linked.open...vai/riv/dodaniDat
http://linked.open...aciTvurceVysledku
http://linked.open.../riv/druhVysledku
http://linked.open...iv/duvernostUdaju
http://linked.open...titaPredkladatele
http://linked.open...dnocenehoVysledku
  • 434395
http://linked.open...ai/riv/idVysledku
  • RIV/68081723:_____/07:00094702
http://linked.open...riv/jazykVysledku
http://linked.open.../riv/klicovaSlova
  • eurofer steel; fatigue; crack propagation (en)
http://linked.open.../riv/klicoveSlovo
http://linked.open...ontrolniKodProRIV
  • [C38E6EDCF69B]
http://linked.open...in/vavai/riv/obor
http://linked.open...ichTvurcuVysledku
http://linked.open...cetTvurcuVysledku
http://linked.open...UplatneniVysledku
http://linked.open...iv/tvurceVysledku
  • Hutař, Pavel
  • Kruml, Tomáš
  • Náhlík, Luboš
  • Obrtlík, Karel
  • Petrenec, Martin
  • Seitl, Stanislav
http://linked.open...n/vavai/riv/zamer
Faceted Search & Find service v1.16.118 as of Jun 21 2024


Alternative Linked Data Documents: ODE     Content Formats:   [cxml] [csv]     RDF   [text] [turtle] [ld+json] [rdf+json] [rdf+xml]     ODATA   [atom+xml] [odata+json]     Microdata   [microdata+json] [html]    About   
This material is Open Knowledge   W3C Semantic Web Technology [RDF Data] Valid XHTML + RDFa
OpenLink Virtuoso version 07.20.3240 as of Jun 21 2024, on Linux (x86_64-pc-linux-gnu), Single-Server Edition (126 GB total memory, 31 GB memory in use)
Data on this page belongs to its respective rights holders.
Virtuoso Faceted Browser Copyright © 2009-2024 OpenLink Software