| - Cyclic strain control tests have been performed on cylindrical specimens of cast polycrystalline Inconel 792-5A superalloy at 23, 500, 700 and 800 °C in laboratory atmosphere to study the effect of temperature on the fatigue behavior. Cyclic hardening-softening curves and fatigue life curves were measured. Scanning electron microscopy was used to investigate the surface relief. Low amplitude straining was characterized by saturation of the stress amplitude. In room temperature high amplitude straining cyclic hardening was followed by marked saturation. Pronounced continuous hardening until failure was observed at 500 °C. Initial cyclic hardening was followed by softening at 800 °C. A systematic shift of the Manson-Coffin and of the Basquin curves to lower fatigue lives was found when temperature was increased. Fatigue cracks were observed to initiate from surface slip markings at all temperatures.
- Cyclic strain control tests have been performed on cylindrical specimens of cast polycrystalline Inconel 792-5A superalloy at 23, 500, 700 and 800 °C in laboratory atmosphere to study the effect of temperature on the fatigue behavior. Cyclic hardening-softening curves and fatigue life curves were measured. Scanning electron microscopy was used to investigate the surface relief. Low amplitude straining was characterized by saturation of the stress amplitude. In room temperature high amplitude straining cyclic hardening was followed by marked saturation. Pronounced continuous hardening until failure was observed at 500 °C. Initial cyclic hardening was followed by softening at 800 °C. A systematic shift of the Manson-Coffin and of the Basquin curves to lower fatigue lives was found when temperature was increased. Fatigue cracks were observed to initiate from surface slip markings at all temperatures. (en)
- Byly provedeny cyklické zkoušky v řízení deformace na válcových vzorcích lité polykrystalické superslitiny Inconel 792-5A, při teplotách 23, 500, 700 a 800 °C v laboratorní atmosféře, za účelem studia vlivu teploty na únavové chování. Byly naměřeny křivky cyklické zpevnění-změkčení a únavové křivky života. K pozorování povrchového reliéfu byl použit řádkovací elektronový mikroskop. Při zatěžování nízkými amplitudami deformace docházelo k saturaci amplitudy napětí. Při pokojové teplotě, cyklickým zatěžováním vysokými amplitudami deformace bylo zpevnění následováno výraznou saturací. Značné kontinuální zpevnění až do lomu bylo pozorováno při teplotě 500 °C. Při 800 °C bylo počáteční cyklické zpevnění následováno změkčením. Při vzrůstu teploty byl zjištěn systematický posuv Manson-Coffinovy a Basquinovy křivek k menším životnostem. Pozorované únavové trhliny iniciovali z povrchových skluzových stop u všech teplot. (cs)
|
| Title
| - Effect of Temperature on the Low Cycle Fatigue of Cast Inconel 792-5A
- Vliv teploty na nízkocyklovou únavu litého Inconelu 792-5A (cs)
- Effect of Temperature on the Low Cycle Fatigue of Cast Inconel 792-5A (en)
|
| skos:prefLabel
| - Effect of Temperature on the Low Cycle Fatigue of Cast Inconel 792-5A
- Vliv teploty na nízkocyklovou únavu litého Inconelu 792-5A (cs)
- Effect of Temperature on the Low Cycle Fatigue of Cast Inconel 792-5A (en)
|
| skos:notation
| - RIV/68081723:_____/07:00093179!RIV08-AV0-68081723
|
| http://linked.open.../vavai/riv/strany
| |
| http://linked.open...avai/riv/aktivita
| |
| http://linked.open...avai/riv/aktivity
| - P(1QS200410502), P(GA106/07/1507), P(GP106/05/P521), Z(AV0Z20410507)
|
| http://linked.open...iv/cisloPeriodika
| |
| http://linked.open...vai/riv/dodaniDat
| |
| http://linked.open...aciTvurceVysledku
| |
| http://linked.open.../riv/druhVysledku
| |
| http://linked.open...iv/duvernostUdaju
| |
| http://linked.open...titaPredkladatele
| |
| http://linked.open...dnocenehoVysledku
| |
| http://linked.open...ai/riv/idVysledku
| - RIV/68081723:_____/07:00093179
|
| http://linked.open...riv/jazykVysledku
| |
| http://linked.open.../riv/klicovaSlova
| - Low cycle fatigue; high temperatures; superalloy; Fatigue life curves; slip markings (en)
|
| http://linked.open.../riv/klicoveSlovo
| |
| http://linked.open...odStatuVydavatele
| - CH - Švýcarská konfederace
|
| http://linked.open...ontrolniKodProRIV
| |
| http://linked.open...i/riv/nazevZdroje
| - Key Engineering Materials
|
| http://linked.open...in/vavai/riv/obor
| |
| http://linked.open...ichTvurcuVysledku
| |
| http://linked.open...cetTvurcuVysledku
| |
| http://linked.open...vavai/riv/projekt
| |
| http://linked.open...UplatneniVysledku
| |
| http://linked.open...v/svazekPeriodika
| |
| http://linked.open...iv/tvurceVysledku
| - Man, Jiří
- Obrtlík, Karel
- Petrenec, Martin
- Polák, Jaroslav
|
| http://linked.open...n/vavai/riv/zamer
| |
| issn
| |
| number of pages
| |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)