| - In this paper, the results of measurements of chemical diffusion of Mn and C in weldments of alloys Fe-0,3%C-5%Mn / Fe-0,3%C-15%Mn are reported. Alloys were cast in induction furnace under protective Ar atmosphere. They were hot-forged to rods of diameter 15mm and cut into pieces of 4mm thickness. These cylindrical samples were metalographical polished. Diffusion couples, welded by electrical impulse, were sealed together with Ti-chips, into evacuated silica ampoules. After that, they were annealed at 1100-800 °C for 1.5-96 hours respectively. Measurement of C redistribution was done in a normal direction to welding interface using electron-scanning microscope Philips SEM-505WDS equipped with Microspec WDX-2A. Diffusion coefficients of C and Mn were obtained and the relations between them were found. (en)
- Příspěvek obsahuje výsledky měření difúze C a Mn ve svarových spojích slitin Fe-0,3%C-5%Mn / Fe-0,3%C-15%Mn. Slitiny byly odlity v laboratorní indukční peci v ochranné atmosféře Ar. Ingoty byly vykovány do tvaru tyčí kruhového průřezu o průměru cca 15mm a homogenizačně žíhány. Po tepelném zpracování byly obrobeny na průměr 12mm a rozřezány na tloušťku 4mm. Vzorky byly metalograficky leštěny a svařeny elektrickým šokem. Difúzní páry byly ve vakuu zataveny do křemenných ampulí společně s titanovými třískami. Byly žíhány při teplotách 1100-800°C po dobu 1,5-96h. Měření redistribuce uhlíku bylo provedeno pomocí úsečkové vlnově disperzní mikroanalýzy na rastrovacím mikroskopu Philips SEM-505 s analyzátorem Microspec WDX-2A ve směru kolmém na svarové rozhraní. Byly stanoveny difúzní koeficienty uhlíku a manganu a objasněny vztahy mezi nimi.
- Příspěvek obsahuje výsledky měření difúze C a Mn ve svarových spojích slitin Fe-0,3%C-5%Mn / Fe-0,3%C-15%Mn. Slitiny byly odlity v laboratorní indukční peci v ochranné atmosféře Ar. Ingoty byly vykovány do tvaru tyčí kruhového průřezu o průměru cca 15mm a homogenizačně žíhány. Po tepelném zpracování byly obrobeny na průměr 12mm a rozřezány na tloušťku 4mm. Vzorky byly metalograficky leštěny a svařeny elektrickým šokem. Difúzní páry byly ve vakuu zataveny do křemenných ampulí společně s titanovými třískami. Byly žíhány při teplotách 1100-800°C po dobu 1,5-96h. Měření redistribuce uhlíku bylo provedeno pomocí úsečkové vlnově disperzní mikroanalýzy na rastrovacím mikroskopu Philips SEM-505 s analyzátorem Microspec WDX-2A ve směru kolmém na svarové rozhraní. Byly stanoveny difúzní koeficienty uhlíku a manganu a objasněny vztahy mezi nimi. (cs)
|
Title
| - Difúze C ve svarovém spoji Fe-0,3C-5Mn/Fe-0,3C-15Mn
- Diffusion of C and Mn in steel weldment Fe-0.3C-5Mn/Fe-0.3C-15Mn (en)
- Difúze C ve svarovém spoji Fe-0,3C-5Mn/Fe-0,3C-15Mn (cs)
|
skos:prefLabel
| - Difúze C ve svarovém spoji Fe-0,3C-5Mn/Fe-0,3C-15Mn
- Diffusion of C and Mn in steel weldment Fe-0.3C-5Mn/Fe-0.3C-15Mn (en)
- Difúze C ve svarovém spoji Fe-0,3C-5Mn/Fe-0,3C-15Mn (cs)
|
skos:notation
| - RIV/68081723:_____/06:00050632!RIV07-AV0-68081723
|
http://linked.open.../vavai/riv/strany
| |
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(IBS2041105), Z(AV0Z20410507)
|
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/68081723:_____/06:00050632
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - up-hill diffusion; carbon (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Král, Lubomír
- Čermák, Jiří
- Million, Bořivoj
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
http://linked.open...n/vavai/riv/zamer
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| |
https://schema.org/isbn
| |