| - Extremely coarse grained aluminium (99.99 %) was subjected to severe plastic deformation (ECAP) at room temperature using the die that had a 90 angle between the die channels. Using this technique a bulk utlrafine grained material can be prepared. The properties of the ECAP material may considerably differ from properties of material with standard grain size. The microstructure of specimens processed by different number of ECAP passes (up to 12 passes), and after creep testing was examined using a scanning electron microscope (SEM) JEOL 6460 with EBSD ( Electron Backscatter Diffraction). The experimental results show that the banded microstructure of ultrafine grained aluminium after one pass by the ECAP die contains high amount of low angle boundaries ( ~ 95 % ) and these are transformed into high angle boundaries by subsequent ECAP pressing. The microstructure after four passes contains more or less equiaxed grains, but the microstructure is still rather heterogenous. It is clear...
- Extremely coarse grained aluminium (99.99 %) was subjected to severe plastic deformation (ECAP) at room temperature using the die that had a 90 angle between the die channels. Using this technique a bulk utlrafine grained material can be prepared. The properties of the ECAP material may considerably differ from properties of material with standard grain size. The microstructure of specimens processed by different number of ECAP passes (up to 12 passes), and after creep testing was examined using a scanning electron microscope (SEM) JEOL 6460 with EBSD ( Electron Backscatter Diffraction). The experimental results show that the banded microstructure of ultrafine grained aluminium after one pass by the ECAP die contains high amount of low angle boundaries ( ~ 95 % ) and these are transformed into high angle boundaries by subsequent ECAP pressing. The microstructure after four passes contains more or less equiaxed grains, but the microstructure is still rather heterogenous. It is clear... (en)
- Extrémně hrubozrnný hliník (99,99%) byl vystaven intenzivní plastické deformaci (ECAP) při pokojové teplotě a při použití zápustky s úhlem 90° mezi kanály. Tato metoda umožňuje připravit ultrajemnozrnné materiály ve větším objemu. Vlastnosti ECAP materiálů se mohou významně lišit od vlastností materiálů se standardní velikostí zrna. Mikrostruktura vzorků s max. počtem 12 ECAP průchodů a creepovém zatěžování byla analyzována rastrovacím elektronovým mikroskopem (SEM) JEOL 6460 vybaveným EBSD ( difrakcí zpětně odražených elektronů). Experimentální výsledky ukazují, že pásová mikrostruktura po 1 ECAP průchodu obsahuje velký počet maloúhlových hranic (~ 95%), které jsou s dalším počtem průchodů postupně transformovány na velkoúhlové hranice. Mikrostruktura po 4 průchodech obsahuje více méně rovnoosá zrna, ale mikrostruktura je stále heterogenní. Je zřejmé, že největší změny mikrostruktury probíhají do 8 průchodů. Mikrostruktura po 8 průchodech se skládá z rovnoosých zrn a obsahuje velký... (cs)
|
| Title
| - Microstructure/properties relationship in ultrafine grained aluminium processed by ECAP technique
- Vztahy mezi mikrostrukturou a vlastnostmi ultrajemnozrnného hliníku připraveného metodou ECAP (cs)
- Microstructure/properties relationship in ultrafine grained aluminium processed by ECAP technique (en)
|
| skos:prefLabel
| - Microstructure/properties relationship in ultrafine grained aluminium processed by ECAP technique
- Vztahy mezi mikrostrukturou a vlastnostmi ultrajemnozrnného hliníku připraveného metodou ECAP (cs)
- Microstructure/properties relationship in ultrafine grained aluminium processed by ECAP technique (en)
|
| skos:notation
| - RIV/68081723:_____/04:00108275!RIV/2005/AV0/A07005/N
|
| http://linked.open.../vavai/riv/strany
| |
| http://linked.open...avai/riv/aktivita
| |
| http://linked.open...avai/riv/aktivity
| - P(IAA2041301), Z(AV0Z2041904)
|
| http://linked.open...vai/riv/dodaniDat
| |
| http://linked.open...aciTvurceVysledku
| |
| http://linked.open.../riv/druhVysledku
| |
| http://linked.open...iv/duvernostUdaju
| |
| http://linked.open...titaPredkladatele
| |
| http://linked.open...dnocenehoVysledku
| |
| http://linked.open...ai/riv/idVysledku
| - RIV/68081723:_____/04:00108275
|
| http://linked.open...riv/jazykVysledku
| |
| http://linked.open.../riv/klicovaSlova
| |
| http://linked.open.../riv/klicoveSlovo
| |
| http://linked.open...ontrolniKodProRIV
| |
| http://linked.open...v/mistoKonaniAkce
| |
| http://linked.open...i/riv/mistoVydani
| |
| http://linked.open...i/riv/nazevZdroje
| |
| http://linked.open...in/vavai/riv/obor
| |
| http://linked.open...ichTvurcuVysledku
| |
| http://linked.open...cetTvurcuVysledku
| |
| http://linked.open...vavai/riv/projekt
| |
| http://linked.open...UplatneniVysledku
| |
| http://linked.open...iv/tvurceVysledku
| - Dvořák, Jiří
- Král, Petr
- Sklenička, Václav
- Svoboda, Milan
|
| http://linked.open...vavai/riv/typAkce
| |
| http://linked.open.../riv/zahajeniAkce
| |
| http://linked.open...n/vavai/riv/zamer
| |
| number of pages
| |
| http://purl.org/ne...btex#hasPublisher
| |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)