| - It was possible to form successfully the samples from aluminide of the type Fe-40at.%Al-Zr-B by niaxial compression due to heating of forming tools. The initial material was obtained in the form of laboratory castings with highly heterogeneous structure, which made an objective evaluation of structure-forming processes difficult. It was necessary to roll the castings in protective capsules slightly and anneal them at the temperature of 1200 °C for the time that would ensure full recrystallization and homogenization of the formed structure. The samples with homogenized structure were subjected to deformation 0.2 at the temperatures from 900 to 1100 °C and to following isothermal annealing lasting from 0 to 240 s. Microstructure fixed by water cooling was then subjected to structural analyses, which led to obtaining of unique information on kinetics of static recrystallization of the investigated alloy.
- It was possible to form successfully the samples from aluminide of the type Fe-40at.%Al-Zr-B by niaxial compression due to heating of forming tools. The initial material was obtained in the form of laboratory castings with highly heterogeneous structure, which made an objective evaluation of structure-forming processes difficult. It was necessary to roll the castings in protective capsules slightly and anneal them at the temperature of 1200 °C for the time that would ensure full recrystallization and homogenization of the formed structure. The samples with homogenized structure were subjected to deformation 0.2 at the temperatures from 900 to 1100 °C and to following isothermal annealing lasting from 0 to 240 s. Microstructure fixed by water cooling was then subjected to structural analyses, which led to obtaining of unique information on kinetics of static recrystallization of the investigated alloy. (en)
|
Title
| - Static recrystalization of intermetallic compound of the type Fe-40at.%Al-Zr-B
- Static recrystalization of intermetallic compound of the type Fe-40at.%Al-Zr-B (en)
|
skos:prefLabel
| - Static recrystalization of intermetallic compound of the type Fe-40at.%Al-Zr-B
- Static recrystalization of intermetallic compound of the type Fe-40at.%Al-Zr-B (en)
|
skos:notation
| - RIV/61989100:27360/13:86088617!RIV14-GA0-27360___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(ED0040/01/01), P(GAP107/10/0438)
|
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/61989100:27360/13:86088617
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - static recrystallization.; annealing; hot forming; as-cast microstructure; Iron aluminides (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| - METAL 2013 : 22nd International Conference on Metallurgy and Materials : conference proceedings : May 15th - 17th 2013, Hotel Voronez I, Brno Czech Republic, EU [CD-ROM]
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Rusz, Stanislav
- Schindler, Ivo
- Kopeček, Jaromír
- Hanus, Pavel
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| |
https://schema.org/isbn
| |
http://localhost/t...ganizacniJednotka
| |