| - The goal of the experiment is an effort to improve the technological formability of iron aluminides and to find other technological possibilities of forming the aluminides with the aim to contribute to the improvement of inferior formability of iron aluminides. In laboratory conditions the samples of iron aluminides FeAl with the chemical composition in at%: 40.7Al–0.15 C–0.15 Mn–0.272 B–0.0065 Mo–0.15 Ti (remainder Fe) were cast with ultrasound and without annealing. These samples were after heating to 1200°C subsequently hot upseted in different states. The first sample was upseted without bandage by a single reduction, the second sample was upseted with an added circumferential ring by a single reduction, and the third sample was upseted entirely wrapped in a capsule, by a single reduction. The last sample was wrapped in the capsule twice and upseted using five stops. After every reduction the sample was charged into the furnace heated to 1200°C. and annealed for 1 minute.
- The goal of the experiment is an effort to improve the technological formability of iron aluminides and to find other technological possibilities of forming the aluminides with the aim to contribute to the improvement of inferior formability of iron aluminides. In laboratory conditions the samples of iron aluminides FeAl with the chemical composition in at%: 40.7Al–0.15 C–0.15 Mn–0.272 B–0.0065 Mo–0.15 Ti (remainder Fe) were cast with ultrasound and without annealing. These samples were after heating to 1200°C subsequently hot upseted in different states. The first sample was upseted without bandage by a single reduction, the second sample was upseted with an added circumferential ring by a single reduction, and the third sample was upseted entirely wrapped in a capsule, by a single reduction. The last sample was wrapped in the capsule twice and upseted using five stops. After every reduction the sample was charged into the furnace heated to 1200°C. and annealed for 1 minute. (en)
|
Title
| - Prevention of Cracking at Hot Pressing of Iron Aluminide Alloy with Limited Formability
- Prevention of Cracking at Hot Pressing of Iron Aluminide Alloy with Limited Formability (en)
|
skos:prefLabel
| - Prevention of Cracking at Hot Pressing of Iron Aluminide Alloy with Limited Formability
- Prevention of Cracking at Hot Pressing of Iron Aluminide Alloy with Limited Formability (en)
|
skos:notation
| - RIV/61989100:27360/11:86081359!RIV12-GA0-27360___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(GAP107/10/0438), S, Z(MSM6198910015)
|
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/61989100:27360/11:86081359
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - limited formability; upseted; aluminides (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Schindler, Ivo
- Šumšal, Václav
- Šíma, Vladimír
|
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://localhost/t...ganizacniJednotka
| |