| - The corrosion of magnesium alloy AZ91 after different types (solution annealing T4 with cooling in air, water, furnace, without or with aging T6) was compared and evaluated by testing with general condensation of moisture. According to gravimetric methodthe higher corrosion resistance was found out after treatment T4+T6 in comparison with T4. The general corrosion was higher after cooling in water than in air. Mikroscopic small spots under white corrosion product (Mg(OH)2) were observed on the surfaces of samples as well as grain boudary etching in state T4+T6 as a result of microgalvanic corrosion. The relations corrosion attack - alloy structure have been studied too. (en)
- Koroze hořčíkové slitiny AZ91 po různých typech tepelného zpracování (rozpouštěcí žíhání T4 s ochlazením na vzduchu, ve vodě, v peci; se stárnutím T6 nebo bez T6) byly porovnávána a hodnocena na základě zkoušky v kondenzační komoře. Podle gravimetrické metody vyšší korozní odolnost byla zjištěna po zpracování T4 a T6 ve srovnání s T4. Celková koroze byla vyšší po ochlazení ve vodě než ve vzduchu. Pod bílými korozními produkty (Mg(OH)2) byly pozorovány tmavé mikroskopické skvrny (body) na povrchu vzorků a také naleptání hranic zrn ve stavu T4+T6 jako výsledek mikrogalvanické koroze. Souvislosti mezi korozním napadením a strukturou slitiny byly také studovány.
|
Title
| - Vliv tepelného zpracování na korozní vlastnosti slitiny AZ91
- Vliv tepelného zpracování na korozní vlastnosti slitiny AZ91 (cs)
- Influence of thermal treatment on corrosion properties of alloy AZ91. (en)
|
skos:prefLabel
| - Vliv tepelného zpracování na korozní vlastnosti slitiny AZ91
- Vliv tepelného zpracování na korozní vlastnosti slitiny AZ91 (cs)
- Influence of thermal treatment on corrosion properties of alloy AZ91. (en)
|
skos:notation
| - RIV/61989100:27360/03:00008735!RIV/2004/GA0/273604/N
|
http://linked.open.../vavai/riv/strany
| |
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/61989100:27360/03:00008735
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - Mg alloy AZ91, thermal treatment, localized corrosion (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| - Sb. konf. Technológia 2003, Bratislava
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...ocetUcastnikuAkce
| |
http://linked.open...nichUcastnikuAkce
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Lasek, Stanislav
- Čížek, Lubomír
- Pawlica, L.
- Ludvíkova, I.
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| - Slovenská technická univerzita v Bratislave. Strojnícka fakulta
|
https://schema.org/isbn
| |
http://localhost/t...ganizacniJednotka
| |