| - Leucite (KAlSi2O6) is the main crystalline phase in feldspathic dental materials. This work is dealing with synthesis of leucite powder, which can be used for the preparation of dental glass-ceramic composites by subsequent thermal treatment. Newly developed procedure is based on preparation of dental raw material as a mixture of two separate compounds: the crystalline leucite powder prepared at relatively low temperature and a commercial matrix powder. Hydrothermal synthesis of tetragonal leucite particles (KAlSi2O6) with the average size of about 3 μm was developed in our laboratory. The leucite dental raw material was prepared by mixing of 20 wt% of synthetic tetragonal leucite with commercial matrix. Dental composites were prepared from the dental raw material by uniaxial pressing and firing up to 960°C. Dilatometric measurements confirmed that the coefficient of thermal expansion increased by 15% when 20 wt% of the tetragonal leucite was added into the basic matrix. In addition, it was show
- Leucite (KAlSi2O6) is the main crystalline phase in feldspathic dental materials. This work is dealing with synthesis of leucite powder, which can be used for the preparation of dental glass-ceramic composites by subsequent thermal treatment. Newly developed procedure is based on preparation of dental raw material as a mixture of two separate compounds: the crystalline leucite powder prepared at relatively low temperature and a commercial matrix powder. Hydrothermal synthesis of tetragonal leucite particles (KAlSi2O6) with the average size of about 3 μm was developed in our laboratory. The leucite dental raw material was prepared by mixing of 20 wt% of synthetic tetragonal leucite with commercial matrix. Dental composites were prepared from the dental raw material by uniaxial pressing and firing up to 960°C. Dilatometric measurements confirmed that the coefficient of thermal expansion increased by 15% when 20 wt% of the tetragonal leucite was added into the basic matrix. In addition, it was show (en)
- Leucite (KAlSi2O6) is the main crystalline phase in feldspathic dental materials. This work is dealing with synthesis of leucite powder, which can be used for the preparation of dental glass-ceramic composites by subsequent thermal treatment. Newly developed procedure is based on preparation of dental raw material as a mixture of two separate compounds: the crystalline leucite powder prepared at relatively low temperature and a commercial matrix powder. Hydrothermal synthesis of tetragonal leucite particles (KAlSi2O6) with the average size of about 3 μm was developed in our laboratory. The leucite dental raw material was prepared by mixing of 20 wt% of synthetic tetragonal leucite with commercial matrix. Dental composites were prepared from the dental raw material by uniaxial pressing and firing up to 960°C. Dilatometric measurements confirmed that the coefficient of thermal expansion increased by 15% when 20 wt% of the tetragonal leucite was added into the basic matrix. In addition, it was show (cs)
|
| Title
| - Příprava leucitové suroviny pro dentální kompozit
- Příprava leucitové suroviny pro dentální kompozit (cs)
- Preparation of leucite raw material for dental composites (en)
|
| skos:prefLabel
| - Příprava leucitové suroviny pro dentální kompozit
- Příprava leucitové suroviny pro dentální kompozit (cs)
- Preparation of leucite raw material for dental composites (en)
|
| skos:notation
| - RIV/60461373:22310/09:00022481!RIV10-MPO-22310___
|
| http://linked.open...avai/riv/aktivita
| |
| http://linked.open...avai/riv/aktivity
| |
| http://linked.open...vai/riv/dodaniDat
| |
| http://linked.open...aciTvurceVysledku
| |
| http://linked.open.../riv/druhVysledku
| |
| http://linked.open...iv/duvernostUdaju
| |
| http://linked.open...titaPredkladatele
| |
| http://linked.open...dnocenehoVysledku
| |
| http://linked.open...ai/riv/idVysledku
| - RIV/60461373:22310/09:00022481
|
| http://linked.open...riv/jazykVysledku
| |
| http://linked.open.../riv/klicovaSlova
| - leucite; analcime; hydrothermal synthesis; dental materials (en)
|
| http://linked.open.../riv/klicoveSlovo
| |
| http://linked.open...ontrolniKodProRIV
| |
| http://linked.open...v/mistoKonaniAkce
| |
| http://linked.open...i/riv/mistoVydani
| |
| http://linked.open...i/riv/nazevZdroje
| - Proceedings-VIIIth International conference PREPARATION OF CERAMIC MATERIALS
|
| http://linked.open...in/vavai/riv/obor
| |
| http://linked.open...ichTvurcuVysledku
| |
| http://linked.open...cetTvurcuVysledku
| |
| http://linked.open...vavai/riv/projekt
| |
| http://linked.open...UplatneniVysledku
| |
| http://linked.open...iv/tvurceVysledku
| - Kloužková, Alexandra
- Kohoutková, Martina
- Mrázová, Martina
|
| http://linked.open...vavai/riv/typAkce
| |
| http://linked.open.../riv/zahajeniAkce
| |
| number of pages
| |
| http://purl.org/ne...btex#hasPublisher
| - Department of Ceramics, Faculty of Metallurgy, Technical University of Košice
|
| https://schema.org/isbn
| |
| http://localhost/t...ganizacniJednotka
| |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)