| - The dwell of isothermal transformation temperature of austempered nodular cast iron 380 °C was optimized in order to obtain optimum combination of static tensile properties. As suitable technological window the range of the dwells 25 to 120 minutes, in which the stress properties slightly increase and the elongation to fracture slightly decreases. Shorter dwells lead to lower level of all tensile mechanical properties, at longer dwells the elongation to fracture substantially decreases.
- The dwell of isothermal transformation temperature of austempered nodular cast iron 380 °C was optimized in order to obtain optimum combination of static tensile properties. As suitable technological window the range of the dwells 25 to 120 minutes, in which the stress properties slightly increase and the elongation to fracture slightly decreases. Shorter dwells lead to lower level of all tensile mechanical properties, at longer dwells the elongation to fracture substantially decreases. (en)
- Doba prodlevy při teplotě izotermického zušlechtění litiny s kuličkovým grafitem 380 °C byla optimalizována tak, aby bylo dosaženo optimální kombinace statických vlastností v tahu. Jako vhodné technologické okno byl nalezen rozsah prodlev 25 až 120 minut, v němž mírně stoupají napěťové vlastnosti a mírně klesá tažnost. Kratší časy vedou k nižší úrovni všech mechanických vlastností v tahu, při delších časech velmi výrazně klesá tažnost. (cs)
|
Title
| - The optimization of isothermal transformation dwell of the ADI obtained at transformation temperature of 380 °C
- Optimalizace prodlevy izotermické transformace litiny s kuličkovým grafitem při transformační teplotě 380 °C (cs)
- The optimization of isothermal transformation dwell of the ADI obtained at transformation temperature of 380 °C (en)
|
skos:prefLabel
| - The optimization of isothermal transformation dwell of the ADI obtained at transformation temperature of 380 °C
- Optimalizace prodlevy izotermické transformace litiny s kuličkovým grafitem při transformační teplotě 380 °C (cs)
- The optimization of isothermal transformation dwell of the ADI obtained at transformation temperature of 380 °C (en)
|
skos:notation
| - RIV/60162694:G43__/08:#0001931!RIV09-MO0-G43_____
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/60162694:G43__/08:#0001931
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - austempered ductile iron; isothermal transformation dwell; tensile stress properties; elongation to fracture (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| - Materials Structure & Micromechanics of Fracture V
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Kohout, Jan
- Věchet, Stanislav
- Zapletal, Josef
- Hanzlíková, Klára
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open...ain/vavai/riv/wos
| |
http://linked.open.../riv/zahajeniAkce
| |
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| |
https://schema.org/isbn
| |
http://localhost/t...ganizacniJednotka
| |