| - Composite materials are used in a wide range of applications such as automotive, aerospace or power generation industry. Most structural parts are dynamically loaded; thus, fatigue must be taken into consideration during the design process even in the case of composite laminates. The most promising way how to predict the fatigue deterioration and reduce necessary experimental input data at the same time seems to be the micro mechanics of failure. However, even this approach requires necessary experimental input data. This paper deals with the woven fabric E-glass epoxy matrix composite. Static and fatigue test were performed. The influence of aluminium shims attached to the specimen on static mechanical properties and fatigue life is shown. Residual tensile strength and residual longitudinal modulus of the woven fabric laminated composite specimens after cyclic loading were investigated.
- Composite materials are used in a wide range of applications such as automotive, aerospace or power generation industry. Most structural parts are dynamically loaded; thus, fatigue must be taken into consideration during the design process even in the case of composite laminates. The most promising way how to predict the fatigue deterioration and reduce necessary experimental input data at the same time seems to be the micro mechanics of failure. However, even this approach requires necessary experimental input data. This paper deals with the woven fabric E-glass epoxy matrix composite. Static and fatigue test were performed. The influence of aluminium shims attached to the specimen on static mechanical properties and fatigue life is shown. Residual tensile strength and residual longitudinal modulus of the woven fabric laminated composite specimens after cyclic loading were investigated. (en)
|
Title
| - Mechanical properties degradation of a glass fibre laminates under cyclic tension
- Mechanical properties degradation of a glass fibre laminates under cyclic tension (en)
|
skos:prefLabel
| - Mechanical properties degradation of a glass fibre laminates under cyclic tension
- Mechanical properties degradation of a glass fibre laminates under cyclic tension (en)
|
skos:notation
| - RIV/49777513:23210/11:43899233!RIV12-GA0-23210___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(1M0519), P(GAP101/11/0288), P(GD101/08/H068)
|
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/49777513:23210/11:43899233
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - Composite, Woven fabric, Fatigue, Experiment, Residual strength (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| - Proceedings : 49th international scientific conference : Experimental stress analysis 2011
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Laš, Vladislav
- Hraška, Matěj
- Cagáň, Jan
- Měšťánek, Petr
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| |
https://schema.org/isbn
| |
http://localhost/t...ganizacniJednotka
| |