| - The high-temperature oxidation behaviour of Fe–25Al–2Ta (in at.%) has been investigated between 600 and 1000 °C using thermogravimetric analysis (TGA) in synthetic air. After oxidation for 1000 h the scales were analysed by light optical microscopy (LOM), grazing incidents X-ray diffraction (GI-XRD), scanning electron microscopy (SEM), and electron probe microanalysis (EPMA). Between 600 and 800 °C thin adherent oxide scales grew according to a parabolic rate law. At 900 °C parabolic growth was observed for several hundred hours, interrupted by sudden mass gains which are probably caused by cracking of the scales, while at 1000 °C no protective scales formed. The scales are predominantly formed by Al2O3 and minor amounts of Fe2O3. While scales formed between 600 and 800 °C are still adherent after cooling to room temperature, scales formed at higher temperatures spalled during/after cooling, possibly because the Laves phase Fe2Ta formed on the sample surfaces underneath the oxide scales.
- The high-temperature oxidation behaviour of Fe–25Al–2Ta (in at.%) has been investigated between 600 and 1000 °C using thermogravimetric analysis (TGA) in synthetic air. After oxidation for 1000 h the scales were analysed by light optical microscopy (LOM), grazing incidents X-ray diffraction (GI-XRD), scanning electron microscopy (SEM), and electron probe microanalysis (EPMA). Between 600 and 800 °C thin adherent oxide scales grew according to a parabolic rate law. At 900 °C parabolic growth was observed for several hundred hours, interrupted by sudden mass gains which are probably caused by cracking of the scales, while at 1000 °C no protective scales formed. The scales are predominantly formed by Al2O3 and minor amounts of Fe2O3. While scales formed between 600 and 800 °C are still adherent after cooling to room temperature, scales formed at higher temperatures spalled during/after cooling, possibly because the Laves phase Fe2Ta formed on the sample surfaces underneath the oxide scales. (en)
|
Title
| - Oxidation resistance of Fe-25Al-2Ta (at.%) in air
- Oxidation resistance of Fe-25Al-2Ta (at.%) in air (en)
|
skos:prefLabel
| - Oxidation resistance of Fe-25Al-2Ta (at.%) in air
- Oxidation resistance of Fe-25Al-2Ta (at.%) in air (en)
|
skos:notation
| - RIV/46747885:24210/10:#0001613!RIV11-MSM-24210___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/46747885:24210/10:#0001613
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - Iron aluminides (based on Fe3Al); Oxidation at high temperatures (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| - GB - Spojené království Velké Británie a Severního Irska
|
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| |
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://localhost/t...ganizacniJednotka
| |