| - The thermal stability of Al-Fe-Mn-Si foils produced using ARB and subsequent cold rolling was studied and compared with conventionally cold rolled (CCR) counterparts. Significant hardness increase was observed after annealing at 200 degrees C only in the ARB samples and was assigned to an annealing-induced hardening. The CCR foil exhibits higher non-recrystallized fraction and smaller mean lamellae boundary spacing in the temperature interval of 200-250 degrees C than ARB foils. The annealing at 450 degrees C results in identical hardness values and fully recrystallized microstructure of all foils, regardless the method used for their manufacturing. However, the ARB samples show higher stability of the refined substructure than their cold rolled counterparts due to continuous recrystallization occurring in the ARB foils.
- The thermal stability of Al-Fe-Mn-Si foils produced using ARB and subsequent cold rolling was studied and compared with conventionally cold rolled (CCR) counterparts. Significant hardness increase was observed after annealing at 200 degrees C only in the ARB samples and was assigned to an annealing-induced hardening. The CCR foil exhibits higher non-recrystallized fraction and smaller mean lamellae boundary spacing in the temperature interval of 200-250 degrees C than ARB foils. The annealing at 450 degrees C results in identical hardness values and fully recrystallized microstructure of all foils, regardless the method used for their manufacturing. However, the ARB samples show higher stability of the refined substructure than their cold rolled counterparts due to continuous recrystallization occurring in the ARB foils. (en)
- Byla studována tepelná stabilita fólií Al-Fe-Mn-Si připravených metodou ARB a následným válcování za studena a porovnána s konvenčně za studena válcovanými vzorky. Výrazný nárůst tvrdosti po žíhání při teplotě 200 C byl pozorován pouze u vzorků ARB a je připisován jevu zpevnění indukovaném žíháním. Fólie CCR vykazují vyšší nerekrystalizovaný podíl a nižší střední rozteč lamelárních hranic zrn v intervalu žíhacích teplot 200-250 C v porovnání se vzorky ARB. Žíhání při teplotě 450 C vede k identickým hodnotám tvrdosti a k plně rekrystalizované struktuře zrn všech fólií, nezávisle na metodě jejich přípravy . Nicméně, vzorky ARB vykazují vyšší stabilitu zjemněné substruktury než jejich za studena válcované protějšky, a to díky kontinuální rekrystalizaci probíhající ve fóliích ARB. (cs)
|
| Title
| - Thermal Stability of Ultrafine Grains in Al-Fe-Mn-Si Foils Prepared by ARB and Subsequent Rolling
- Tepelná stabilita ultra-jemných zrn ve fóliích Al-Fe-Mn-Si připravených metodou ARB a následným válcováním (cs)
- Thermal Stability of Ultrafine Grains in Al-Fe-Mn-Si Foils Prepared by ARB and Subsequent Rolling (en)
|
| skos:prefLabel
| - Thermal Stability of Ultrafine Grains in Al-Fe-Mn-Si Foils Prepared by ARB and Subsequent Rolling
- Tepelná stabilita ultra-jemných zrn ve fóliích Al-Fe-Mn-Si připravených metodou ARB a následným válcováním (cs)
- Thermal Stability of Ultrafine Grains in Al-Fe-Mn-Si Foils Prepared by ARB and Subsequent Rolling (en)
|
| skos:notation
| - RIV/26316919:_____/08:#0000160!RIV09-MSM-26316919
|
| http://linked.open...avai/riv/aktivita
| |
| http://linked.open...avai/riv/aktivity
| |
| http://linked.open...iv/cisloPeriodika
| |
| http://linked.open...vai/riv/dodaniDat
| |
| http://linked.open...aciTvurceVysledku
| |
| http://linked.open.../riv/druhVysledku
| |
| http://linked.open...iv/duvernostUdaju
| |
| http://linked.open...titaPredkladatele
| |
| http://linked.open...dnocenehoVysledku
| |
| http://linked.open...ai/riv/idVysledku
| - RIV/26316919:_____/08:#0000160
|
| http://linked.open...riv/jazykVysledku
| |
| http://linked.open.../riv/klicovaSlova
| - Thermal stability; accumulative roll bonding (ARB); Al-Fe-Mn-Si alloy; EBSD; TEM (en)
|
| http://linked.open.../riv/klicoveSlovo
| |
| http://linked.open...odStatuVydavatele
| - CH - Švýcarská konfederace
|
| http://linked.open...ontrolniKodProRIV
| |
| http://linked.open...i/riv/nazevZdroje
| |
| http://linked.open...in/vavai/riv/obor
| |
| http://linked.open...ichTvurcuVysledku
| |
| http://linked.open...cetTvurcuVysledku
| |
| http://linked.open...UplatneniVysledku
| |
| http://linked.open...v/svazekPeriodika
| |
| http://linked.open...iv/tvurceVysledku
| - Cieslar, Miroslav
- Sláma, Peter
- Homola, Petr
- Slámová, Margarita
|
| http://linked.open...ain/vavai/riv/wos
| |
| http://linked.open...n/vavai/riv/zamer
| |
| issn
| |
| number of pages
| |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)