| - Ultra-fine grained sheets were prepared by up to six cycles of ARB at ambient temperature from an Al-0.22Sc-0.13Zr alloy in two states: a non-age-hardened and a peak-aged. The effect of Al-3(Sc1-xZrx) precipitates on the thermal stability of the UFG structures produced by ARB was investigated by isochronal annealing. Annealing at 300 degrees C induces an additional strengthening in non-pre-aged ARB material that may be ascribed to precipitation and growth of coherent Al-3(Sc1-xZrx) particles. This result suggests that the hardness decrease introduced by ARB in the peak-aged specimen is due to dissolution of precipitates during deformation. The annealing response of the materials above 300 degrees C does not depend on their thermal pre-treatment. However, the finely dispersed Al-3(Sc1-xZrx) precipitates stabilise the refined deformed microstructure suitable for superplastic forming up to relatively high temperatures.
- Ultra-fine grained sheets were prepared by up to six cycles of ARB at ambient temperature from an Al-0.22Sc-0.13Zr alloy in two states: a non-age-hardened and a peak-aged. The effect of Al-3(Sc1-xZrx) precipitates on the thermal stability of the UFG structures produced by ARB was investigated by isochronal annealing. Annealing at 300 degrees C induces an additional strengthening in non-pre-aged ARB material that may be ascribed to precipitation and growth of coherent Al-3(Sc1-xZrx) particles. This result suggests that the hardness decrease introduced by ARB in the peak-aged specimen is due to dissolution of precipitates during deformation. The annealing response of the materials above 300 degrees C does not depend on their thermal pre-treatment. However, the finely dispersed Al-3(Sc1-xZrx) precipitates stabilise the refined deformed microstructure suitable for superplastic forming up to relatively high temperatures. (en)
- Byly připraveny ultra-jemnozrnné plechy ze slitiny Al-0.22Sc-0.13Zr ve dvou stavech (nevytvrzovaný a maximálně vytvrzený), a to až šesti cykly kumulativního spojování válcováním při pokojové teplotě. Byl studován vliv precipitátů Al-3(Sc1-xZrx) na tepelnou stabilitu ultra-jemnozrnných struktur pomocí izochronního žíhání. Žíhání při 300 C způsobuje další zpevnění před deformací nezpevněného materiálu, což může být připsáno precipitaci a růstu koherentních precipitátů Al-3(Sc1-xZrx). Tento výsledek poukazuje na to, že pokles tvrdosti během deformačního zpracování metodou ARB u vzorku vytvrzeného na maximum je způsoben rozpouštěním precipitátů v průběhu deformace. Tepelná stabilita materiálů nad teplotou 300 C není závislá na způsobu předcházejícího tepelného zpracování. Nicméně, jemně distribuované precipitáty Al-3(Sc1-xZrx) stabilizují zjemněnou deformační mikrostrukturu vhodnou pro superplastické tváření pří relativně vysokých teplotách. (cs)
|
| Title
| - Annealing Response of Al-0.22Sc-0.13Zr Alloy Processed by Accumulative Roll Bonding
- Annealing Response of Al-0.22Sc-0.13Zr Alloy Processed by Accumulative Roll Bonding (en)
- Tepelná stabilita slitiny Al-0.22Sc-0.13Zr připravené metodou kumulativního spojování válcováním (cs)
|
| skos:prefLabel
| - Annealing Response of Al-0.22Sc-0.13Zr Alloy Processed by Accumulative Roll Bonding
- Annealing Response of Al-0.22Sc-0.13Zr Alloy Processed by Accumulative Roll Bonding (en)
- Tepelná stabilita slitiny Al-0.22Sc-0.13Zr připravené metodou kumulativního spojování válcováním (cs)
|
| skos:notation
| - RIV/26316919:_____/08:#0000159!RIV09-MSM-26316919
|
| http://linked.open...avai/riv/aktivita
| |
| http://linked.open...avai/riv/aktivity
| |
| http://linked.open...iv/cisloPeriodika
| |
| http://linked.open...vai/riv/dodaniDat
| |
| http://linked.open...aciTvurceVysledku
| |
| http://linked.open.../riv/druhVysledku
| |
| http://linked.open...iv/duvernostUdaju
| |
| http://linked.open...titaPredkladatele
| |
| http://linked.open...dnocenehoVysledku
| |
| http://linked.open...ai/riv/idVysledku
| - RIV/26316919:_____/08:#0000159
|
| http://linked.open...riv/jazykVysledku
| |
| http://linked.open.../riv/klicovaSlova
| - Thermal stability; accumulative roll bonding (ARB); AlScZr alloy; EBSD; TEM (en)
|
| http://linked.open.../riv/klicoveSlovo
| |
| http://linked.open...odStatuVydavatele
| - CH - Švýcarská konfederace
|
| http://linked.open...ontrolniKodProRIV
| |
| http://linked.open...i/riv/nazevZdroje
| |
| http://linked.open...in/vavai/riv/obor
| |
| http://linked.open...ichTvurcuVysledku
| |
| http://linked.open...cetTvurcuVysledku
| |
| http://linked.open...UplatneniVysledku
| |
| http://linked.open...v/svazekPeriodika
| |
| http://linked.open...iv/tvurceVysledku
| - Cieslar, Miroslav
- Očenášek, Vladivoj
- Homola, Petr
- Slámová, Margarita
- Uhlíř, Jaromír
|
| http://linked.open...ain/vavai/riv/wos
| |
| http://linked.open...n/vavai/riv/zamer
| |
| issn
| |
| number of pages
| |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)