  • The fatigue behaviour of bare and pre-corroded AZ31 magnesium alloy in the stress amplitude control mode was studied. Two sets of test specimens were exposed to corrosion environment prior to fatigue test. Corrosion of test specimens was carried out in a spray of neutral 5% solution of sodium chloride for period of 480 and 1000 hrs. In order to assess the corrosion rate and corrosion mechanism of experimental material, reference specimens were exposed to corrosion environment for period of time ranging from 1 to 1000 hrs. Fatigue tests in the stress amplitude control mode were carried out on smooth and pre-corroded specimens. Analysis of hysteresis curves was preformed. Comparison of cyclic deformation curves showed that cyclic deformation response is not affected by corrosion damage. Experimental data in both, the low and high cycle fatigue regions were fitted by means of regression functions. S-N curves exhibited smooth transition from the low to the high cycle fatigue regions. Presence of corrosion
  • The fatigue behaviour of bare and pre-corroded AZ31 magnesium alloy in the stress amplitude control mode was studied. Two sets of test specimens were exposed to corrosion environment prior to fatigue test. Corrosion of test specimens was carried out in a spray of neutral 5% solution of sodium chloride for period of 480 and 1000 hrs. In order to assess the corrosion rate and corrosion mechanism of experimental material, reference specimens were exposed to corrosion environment for period of time ranging from 1 to 1000 hrs. Fatigue tests in the stress amplitude control mode were carried out on smooth and pre-corroded specimens. Analysis of hysteresis curves was preformed. Comparison of cyclic deformation curves showed that cyclic deformation response is not affected by corrosion damage. Experimental data in both, the low and high cycle fatigue regions were fitted by means of regression functions. S-N curves exhibited smooth transition from the low to the high cycle fatigue regions. Presence of corrosion (en)
Title
  • Influence of Corrosion Damage on Fatigue Behaviour of AZ31 Magnesium Alloy
  • Influence of Corrosion Damage on Fatigue Behaviour of AZ31 Magnesium Alloy (en)
skos:prefLabel
  • Influence of Corrosion Damage on Fatigue Behaviour of AZ31 Magnesium Alloy
  • Influence of Corrosion Damage on Fatigue Behaviour of AZ31 Magnesium Alloy (en)
skos:notation
  • RIV/00216305:26210/13:PU107354!RIV14-MSM-26210___
http://linked.open...avai/riv/aktivita
http://linked.open...avai/riv/aktivity
  • S
http://linked.open...vai/riv/dodaniDat
http://linked.open...aciTvurceVysledku
http://linked.open.../riv/druhVysledku
http://linked.open...iv/duvernostUdaju
http://linked.open...titaPredkladatele
http://linked.open...dnocenehoVysledku
  • 79710
http://linked.open...ai/riv/idVysledku
  • RIV/00216305:26210/13:PU107354
http://linked.open...riv/jazykVysledku
http://linked.open.../riv/klicovaSlova
  • magnesium alloy, corrosion, fatigue (en)
http://linked.open.../riv/klicoveSlovo
http://linked.open...ontrolniKodProRIV
  • [0FC97D0707A5]
http://linked.open...in/vavai/riv/obor
http://linked.open...ichTvurcuVysledku
http://linked.open...cetTvurcuVysledku
http://linked.open...UplatneniVysledku
http://linked.open...iv/tvurceVysledku
  • Doležal, Pavel
  • Gejdoš, Pavel
  • Horynová, Miroslava
  • Zapletal, Josef
  • Modráčková, Ivana
http://localhost/t...ganizacniJednotka
  • 26210
Faceted Search & Find service v1.16.118 as of Jun 21 2024


Alternative Linked Data Documents: ODE     Content Formats:   [cxml] [csv]     RDF   [text] [turtle] [ld+json] [rdf+json] [rdf+xml]     ODATA   [atom+xml] [odata+json]     Microdata   [microdata+json] [html]    About   
This material is Open Knowledge   W3C Semantic Web Technology [RDF Data] Valid XHTML + RDFa
OpenLink Virtuoso version 07.20.3240 as of Jun 21 2024, on Linux (x86_64-pc-linux-gnu), Single-Server Edition (126 GB total memory, 106 GB memory in use)
Data on this page belongs to its respective rights holders.
Virtuoso Faceted Browser Copyright © 2009-2024 OpenLink Software