| - The electrophoretic deposition of alumina and zirconia powders in the constant-current regime was studied. The method of direct weight measurement of deposition kinetics was used. The electric current during deposition in range 250 microA - 48 miliA were used. The density and hardness measurements were performed. The intensity of electric field and measured values were compared. It was found that with increasing electric field decreases the density of deposits after annealing, as well as hardness of deposits after sintering. Thanks to the precise description of kinetics electrophoretoc deposition the microlaminate consisting alternating 75 layers of alumina and 75 layers of zirconia was prepared. (en)
- Metoda elektroforetické depozice byla použita pro přípravu monolitických keramických struktur na bázi oxidu hlinitého a oxidu zirkoničitého. Dále byla tato metoda použita pro přípravu vrstevnaté struktury ze stejných materiálů. Byly připraveny koloidní suspenze, z nichž byla tvarována keramická tělesa při různých proudových hustotách v rozsahu 250 mikroA - 48 miliA. Kinetika elektroforetické depozice byla popsána přímým měřením hmotnosti depozitu. Po tepelném a keramografickém zpracování byly depozity studovány z hlediska fyzikálních a mechanických vlastností. Bylo zjištěno, že výslená hustota po žíhání a slinování se s rostoucím elektrickým polem snižuje, což bylo potvrzeno při následném měření tvrdosti keramických těles. Díky zlepšenému popisu kinetiky elektroforetické depozice byla připravena vrstevnatá struktura sestávající z 75 vrstev oxidu hliného a 75 vrstev oxidu zirkoničitého.
- Metoda elektroforetické depozice byla použita pro přípravu monolitických keramických struktur na bázi oxidu hlinitého a oxidu zirkoničitého. Dále byla tato metoda použita pro přípravu vrstevnaté struktury ze stejných materiálů. Byly připraveny koloidní suspenze, z nichž byla tvarována keramická tělesa při různých proudových hustotách v rozsahu 250 mikroA - 48 miliA. Kinetika elektroforetické depozice byla popsána přímým měřením hmotnosti depozitu. Po tepelném a keramografickém zpracování byly depozity studovány z hlediska fyzikálních a mechanických vlastností. Bylo zjištěno, že výslená hustota po žíhání a slinování se s rostoucím elektrickým polem snižuje, což bylo potvrzeno při následném měření tvrdosti keramických těles. Díky zlepšenému popisu kinetiky elektroforetické depozice byla připravena vrstevnatá struktura sestávající z 75 vrstev oxidu hliného a 75 vrstev oxidu zirkoničitého. (cs)
|
| Title
| - Vliv podmínek elektroforetické depozice na konečné vlastnosti Al2O3 a ZrO2 keramik
- Vliv podmínek elektroforetické depozice na konečné vlastnosti Al2O3 a ZrO2 keramik (cs)
- Final Properties of Alumina and Zirconia Ceramics Prepared via Electrophoretic Deposition (en)
|
| skos:prefLabel
| - Vliv podmínek elektroforetické depozice na konečné vlastnosti Al2O3 a ZrO2 keramik
- Vliv podmínek elektroforetické depozice na konečné vlastnosti Al2O3 a ZrO2 keramik (cs)
- Final Properties of Alumina and Zirconia Ceramics Prepared via Electrophoretic Deposition (en)
|
| skos:notation
| - RIV/00216305:26210/10:PU91672!RIV11-MSM-26210___
|
| http://linked.open...avai/riv/aktivita
| |
| http://linked.open...avai/riv/aktivity
| |
| http://linked.open...vai/riv/dodaniDat
| |
| http://linked.open...aciTvurceVysledku
| |
| http://linked.open.../riv/druhVysledku
| |
| http://linked.open...iv/duvernostUdaju
| |
| http://linked.open...titaPredkladatele
| |
| http://linked.open...dnocenehoVysledku
| |
| http://linked.open...ai/riv/idVysledku
| - RIV/00216305:26210/10:PU91672
|
| http://linked.open...riv/jazykVysledku
| |
| http://linked.open.../riv/klicovaSlova
| - Electrophoretic deposition, alumina, zirconia (en)
|
| http://linked.open.../riv/klicoveSlovo
| |
| http://linked.open...ontrolniKodProRIV
| |
| http://linked.open...v/mistoKonaniAkce
| |
| http://linked.open...i/riv/mistoVydani
| |
| http://linked.open...i/riv/nazevZdroje
| - Víceúrovňový design pokrokových materiálů 2010
|
| http://linked.open...in/vavai/riv/obor
| |
| http://linked.open...ichTvurcuVysledku
| |
| http://linked.open...cetTvurcuVysledku
| |
| http://linked.open...UplatneniVysledku
| |
| http://linked.open...iv/tvurceVysledku
| - Hadraba, Hynek
- Maca, Karel
- Drdlík, Daniel
|
| http://linked.open...vavai/riv/typAkce
| |
| http://linked.open.../riv/zahajeniAkce
| |
| http://linked.open...n/vavai/riv/zamer
| |
| number of pages
| |
| http://purl.org/ne...btex#hasPublisher
| - Ústav fyziky materiálů AV ČR
|
| https://schema.org/isbn
| |
| http://localhost/t...ganizacniJednotka
| |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)