| - The dissimilar laboratory welds of bainitic T25 steel, currently being developed, and modified martensitic chromium P91 steel have been subject of study. Both base materials were ion-nitrided and homogenized at 1050 st.C/24h before welding. The redistribution of interstitials (C, N) and phase profiles in the weld joints were simulated using DICTRA software package at different annealing conditions of 600 st.C/240h and 900 st./18h. The results from the simulation were compared with experimental observations. A relatively good agreement between the simulation and the experiments was observed
- The dissimilar laboratory welds of bainitic T25 steel, currently being developed, and modified martensitic chromium P91 steel have been subject of study. Both base materials were ion-nitrided and homogenized at 1050 st.C/24h before welding. The redistribution of interstitials (C, N) and phase profiles in the weld joints were simulated using DICTRA software package at different annealing conditions of 600 st.C/240h and 900 st./18h. The results from the simulation were compared with experimental observations. A relatively good agreement between the simulation and the experiments was observed (en)
- Předmětem našeho studia je heterogenní svarový spoj nově vyvíjené bainitické oceli T25 s modifikovanou martenzitickou chromovou ocelí P91. Oba základní materiály byly před svařením iontově nitridovány a následně homogenizovány při 1050 st.C/24h. Pomocí programu DICTRA byly provedeny simulace rozdělení intersticiálních prvků (uhlíku a dusíku) a fázových profilů ve svarovém spoji při podmínkách žíhání 600 st.C/240h a 900 st.C/18h. Vypočtené závislosti byly porovnány s experimentálně získanými výsledky. Výsledky počítačové simulace jsou ve velmi dobré shodě s experimentem. (cs)
|
Title
| - Microstructural Stability of Dissimilar Weld Joint of Creep-Resistant Steels with Increased Content at 500-900 st.C
- Stabilita mikrostruktury heterogenních svarových spojů žáropevných ocelí se zvýšeným obsahem dusíku při 500-900 st. C (cs)
- Microstructural Stability of Dissimilar Weld Joint of Creep-Resistant Steels with Increased Content at 500-900 st.C (en)
|
skos:prefLabel
| - Microstructural Stability of Dissimilar Weld Joint of Creep-Resistant Steels with Increased Content at 500-900 st.C
- Stabilita mikrostruktury heterogenních svarových spojů žáropevných ocelí se zvýšeným obsahem dusíku při 500-900 st. C (cs)
- Microstructural Stability of Dissimilar Weld Joint of Creep-Resistant Steels with Increased Content at 500-900 st.C (en)
|
skos:notation
| - RIV/00216305:26210/07:PU69293!RIV08-MSM-26210___
|
http://linked.open.../vavai/riv/strany
| |
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/00216305:26210/07:PU69293
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - creep-resistant steel, weld joints, structural analyses, thermodynamic and kinetic modelling, carbon and nitrogen redistribution (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| - CH - Švýcarská konfederace
|
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| - Defect and Diffusion Forum
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Buršík, Jiří
- Foret, Rudolf
- Svoboda, Milan
- Zlámal, Bronislav
|
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://localhost/t...ganizacniJednotka
| |