| - Stabillity loss during displacement-controlled loading is possible due to the low rigidity of the loading machine (loading set-up). This stability loss appears as a jump in measured parameters (catastrophe), while needed dependency is not obtained. Here, a procedure is used for recognition of this problem and its correction in the case of fracture tests on specimens of selected cement-based composite. The reasons for overestimation of fracture energy evaluated from load-deflection diagrams without correction are indicated in the paper.
- Stabillity loss during displacement-controlled loading is possible due to the low rigidity of the loading machine (loading set-up). This stability loss appears as a jump in measured parameters (catastrophe), while needed dependency is not obtained. Here, a procedure is used for recognition of this problem and its correction in the case of fracture tests on specimens of selected cement-based composite. The reasons for overestimation of fracture energy evaluated from load-deflection diagrams without correction are indicated in the paper. (en)
- Stabillity loss during displacement-controlled loading is possible due to the low rigidity of the loading machine (loading set-up). This stability loss appears as a jump in measured parameters (catastrophe), while needed dependency is not obtained. Here, a procedure is used for recognition of this problem and its correction in the case of fracture tests on specimens of selected cement-based composite. The reasons for overestimation of fracture energy evaluated from load-deflection diagrams without correction are indicated in the paper. (cs)
|
Title
| - Accepting of influence of stability loss during displacement-controlled loading in fracture test
- Accepting of influence of stability loss during displacement-controlled loading in fracture test (en)
- Accepting of influence of stability loss during displacement-controlled loading in fracture test (cs)
|
skos:prefLabel
| - Accepting of influence of stability loss during displacement-controlled loading in fracture test
- Accepting of influence of stability loss during displacement-controlled loading in fracture test (en)
- Accepting of influence of stability loss during displacement-controlled loading in fracture test (cs)
|
skos:notation
| - RIV/00216305:26110/07:PU69214!RIV08-MSM-26110___
|
http://linked.open.../vavai/riv/strany
| |
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(1M06005), P(GA103/07/1276)
|
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/00216305:26110/07:PU69214
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - Fracture test, cement-based composite, fracture energy (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| - Ecology and new building materials and products
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Frantík, Petr
- Keršner, Zbyněk
- Veselý, Václav
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| |
https://schema.org/isbn
| |
http://localhost/t...ganizacniJednotka
| |