| - Large (cm x cm), uniform-thickness areas of an inverse-opal photonic crystal and an inverse-opal monolayer were fabricated in a high-refractive-index As30S70 chalcogenide glass. We have developed an effective low-cost, solution-based process for fabrication of photonic structures in chalcogenide glass from silica-colloidal-crystal thin-film templates (multi- and monolayer). The chalcogenide-glass solution is spin-coated over the silica-opal film template and the infilled composite structure (chalcogenide/opal) is then lifted-off and transferred onto the chalcogenide-glass disc at 225 C, followed by removal of the template in hydrofluoric acid. The extra step introduced in this work (lift-off and transfer) allows a reproducible and large-area structure to be fabricated on a bulk chalcogenide glass. Complete infilling of the silica template is possible due to the nano-colloidal nature (particle size 2-8 nm) of the chalcogenide-glass solution and effective solvent release from the spin-coated chalcogenide film during post-annealing. The resulting chalcogenide-glass inverse-opal multilayer exhibits a Bragg peak at 670 nm with a reflectance 70%, while the inverse-opal monolayer shows anti-reflectance behaviour {2% in the near-infrared region (1215-1660 nm).
- Large (cm x cm), uniform-thickness areas of an inverse-opal photonic crystal and an inverse-opal monolayer were fabricated in a high-refractive-index As30S70 chalcogenide glass. We have developed an effective low-cost, solution-based process for fabrication of photonic structures in chalcogenide glass from silica-colloidal-crystal thin-film templates (multi- and monolayer). The chalcogenide-glass solution is spin-coated over the silica-opal film template and the infilled composite structure (chalcogenide/opal) is then lifted-off and transferred onto the chalcogenide-glass disc at 225 C, followed by removal of the template in hydrofluoric acid. The extra step introduced in this work (lift-off and transfer) allows a reproducible and large-area structure to be fabricated on a bulk chalcogenide glass. Complete infilling of the silica template is possible due to the nano-colloidal nature (particle size 2-8 nm) of the chalcogenide-glass solution and effective solvent release from the spin-coated chalcogenide film during post-annealing. The resulting chalcogenide-glass inverse-opal multilayer exhibits a Bragg peak at 670 nm with a reflectance 70%, while the inverse-opal monolayer shows anti-reflectance behaviour {2% in the near-infrared region (1215-1660 nm). (en)
|
Title
| - Large-area inverse opal structures in a bulk chalcogenide glass by spin-coating and thin-film transfer
- Large-area inverse opal structures in a bulk chalcogenide glass by spin-coating and thin-film transfer (en)
|
skos:prefLabel
| - Large-area inverse opal structures in a bulk chalcogenide glass by spin-coating and thin-film transfer
- Large-area inverse opal structures in a bulk chalcogenide glass by spin-coating and thin-film transfer (en)
|
skos:notation
| - RIV/00216275:25310/13:39896950!RIV14-MSM-25310___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/00216275:25310/13:39896950
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - spin-coating; photonic structures; inverse opal; chalcogenide glasses (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Kohoutek, Tomáš
- Orava, Jiří
- Wágner, Tomáš
- Střižík, Lukáš
- Greer, A. L.
- Bardosova, M.
- Fudouzi, H.
|
http://linked.open...ain/vavai/riv/wos
| |
issn
| |
number of pages
| |
http://bibframe.org/vocab/doi
| - 10.1016/j.optmat.2013.09.026
|
http://localhost/t...ganizacniJednotka
| |