| - The phase diagrams of the {Ta,V}-Sb systems have been investigated by XRPD, LOM, EPMA, and DTA in closed quartz ampoules up 1050°C, and in sealed Ta crucibles up to 1450°C. The results were compared with the previously established Nb-Sb system. The result from Melnyk et al. was confirmed in this investigation since it is in very good agreement with our investigation. The following binary phases in the Ta-Sb systems: Ta3Sb, Ta5Sb4, and TaSb2 were found to be stable at 900°C. For the V-Sb system, additional binary phases are present and their mechanism of formation is different from that of the {Ta,Nb}-Sb systems. Diffusion couple experiment between V-VSb2 revealed that the following binary phases are stable at 800°C: V3Sb, V3Sb2 (ht), V7.46Sb9, and VSb2. The phase V5Sb4 previously known in the literature was found to be stable below 800°C. In contrast to the {Ta,Nb}-Sb system, only V3Sb, V3Sb2, and VSb2 were found in as cast state, which indicates peritectic formation. The other phases, V7.
- The phase diagrams of the {Ta,V}-Sb systems have been investigated by XRPD, LOM, EPMA, and DTA in closed quartz ampoules up 1050°C, and in sealed Ta crucibles up to 1450°C. The results were compared with the previously established Nb-Sb system. The result from Melnyk et al. was confirmed in this investigation since it is in very good agreement with our investigation. The following binary phases in the Ta-Sb systems: Ta3Sb, Ta5Sb4, and TaSb2 were found to be stable at 900°C. For the V-Sb system, additional binary phases are present and their mechanism of formation is different from that of the {Ta,Nb}-Sb systems. Diffusion couple experiment between V-VSb2 revealed that the following binary phases are stable at 800°C: V3Sb, V3Sb2 (ht), V7.46Sb9, and VSb2. The phase V5Sb4 previously known in the literature was found to be stable below 800°C. In contrast to the {Ta,Nb}-Sb system, only V3Sb, V3Sb2, and VSb2 were found in as cast state, which indicates peritectic formation. The other phases, V7. (en)
|
Title
| - Constitution of the systems {Ta,Nb,V}-Sb in the Sb-rich part (> 50 at.% Sb)
- Constitution of the systems {Ta,Nb,V}-Sb in the Sb-rich part (> 50 at.% Sb) (en)
|
skos:prefLabel
| - Constitution of the systems {Ta,Nb,V}-Sb in the Sb-rich part (> 50 at.% Sb)
- Constitution of the systems {Ta,Nb,V}-Sb in the Sb-rich part (> 50 at.% Sb) (en)
|
skos:notation
| - RIV/00216224:14740/14:00076496!RIV15-MSM-14740___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(7AMB13AT019), P(ED1.1.00/02.0068)
|
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/00216224:14740/14:00076496
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - thermoelectrics; phase diagram; thermal analysis; X-ray analysis; electron microscopy (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Brož, Pavel
- Grytsiv, Andrei
- Rogl, Peter Franz
- Failamani, Fainan
- Maccio, Daniele
- Saccone, Adriana
|
http://localhost/t...ganizacniJednotka
| |