| - Formation of corrosion products on hot-dip galvanised steel (HDG), Zn-5Al, Zn-11Al-3Mg-0.2Si, Zn-16Mg and Zn-1.5Al-1.5Mg with pre-deposited NaCl was followed in humid air at 20 C. The alloyed coatings showed an improvement in mass loss by a factor of 4-7 to HDG. Corrosion products on the alloyed coatings contained twice as much carbonates than those formed on HDG. Magnesium dissolved preferentially, and aluminium-enriched phases were the most stable. Magnesium buffered the pH at cathodic sites, thus hindering the formation of zinc oxide and inhibiting the oxygen reduction. Magnesium products at the metal/corrosion product interface might also have an inhibiting effect.
- Formation of corrosion products on hot-dip galvanised steel (HDG), Zn-5Al, Zn-11Al-3Mg-0.2Si, Zn-16Mg and Zn-1.5Al-1.5Mg with pre-deposited NaCl was followed in humid air at 20 C. The alloyed coatings showed an improvement in mass loss by a factor of 4-7 to HDG. Corrosion products on the alloyed coatings contained twice as much carbonates than those formed on HDG. Magnesium dissolved preferentially, and aluminium-enriched phases were the most stable. Magnesium buffered the pH at cathodic sites, thus hindering the formation of zinc oxide and inhibiting the oxygen reduction. Magnesium products at the metal/corrosion product interface might also have an inhibiting effect. (en)
|
Title
| - Composition of corrosion products formed on Zn-Mg, Zn-Al and Zn-Al-Mg coatings in model atmospheric conditions
- Composition of corrosion products formed on Zn-Mg, Zn-Al and Zn-Al-Mg coatings in model atmospheric conditions (en)
|
skos:prefLabel
| - Composition of corrosion products formed on Zn-Mg, Zn-Al and Zn-Al-Mg coatings in model atmospheric conditions
- Composition of corrosion products formed on Zn-Mg, Zn-Al and Zn-Al-Mg coatings in model atmospheric conditions (en)
|
skos:notation
| - RIV/60461373:22310/14:43898184!RIV15-MSM-22310___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/60461373:22310/14:43898184
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - Metal coatings, Zinc, Weight loss, Atmospheric corrosion (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| - GB - Spojené království Velké Británie a Severního Irska
|
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Stoulil, Jan
- Thierry, D.
- Prošek, Tomáš
- Petterson, D.
|
http://linked.open...ain/vavai/riv/wos
| |
issn
| |
number of pages
| |
http://bibframe.org/vocab/doi
| - 10.1016/j.corsci.2014.05.016
|
http://localhost/t...ganizacniJednotka
| |