Existing methods for life prediction of components are often not reliable and high safety factors must be used. Recent research into fatigue damage of structural materials revealed new possibilities to evaluate the fatigue life based not only on the stress amplitude but on the plastic strain amplitude. It is important to use a differential characteristic, the growth rate of short cracks Within a proposed project new findings concerning the effect of plastic strain amplitude and mean stress will be obtained. The rates of short cracks will be measured and the kinetics of short crack growth for various values of plastic strain amplitudes and mean stresses will be established. Simultaneously the fatigue life of smooth specimens cycled with various plastic strain amplitudes and mean stresses will be determined and correlated with the rates of short crack in order to propose more simple evaluation of relevant parameters. (en)
Dosavadní postupy predikce únavové životnosti strojních součástí nejsou spolehlivé a často vedou k vysokým koeficientům bezpečnosti. Nedávné výzkumy únavového poškození konstrukčních materiálů ukázaly nové možnosti odhadu únavové životnosti založené nejen na amplitudě napětí ale na znalosti amplitudy plastické deformace. Aplikací diferenciální charakteristiky, rychlosti růstu krátkých únavových trhlin lze odhadnout únavovou životnost mnohem přesněji. V rámci navrhovaného projektu budou získány novépoznatky o vlivu amplitudy plastické deformace a současně středního napětí v cyklu nutné pro aplikaci nových principů predikce životnosti. Budou měřeny rychlosti šíření krátkých trhlin a určena závislost kinetiky šíření na amplitudě plastické deformace a na středním napětí. Zároveň budou provedena experimentální měření životnosti hladkých vzorků pro různé hodnoty amplitudy plastické deformace a střední napětí s cílem vzájemně korelovat životnosti a rychlosti šíření trhlin a umožnit jednodušší (cs)