| - High-cycle fatigue/creep behaviour of cast nickel base superalloy IN713LC was experimentally examined at 800 C in air. Experiments were aimed on determination of cyclic creep rate, time to fracture, kind and mode of damage. An attempt has been made to explain the cyclic creep behaviour by a balance between an effect of decrease of plastic strain response with increasing strain rate in a loading cycle and an accelerating effect of the cyclic plasticity on the development of unidirectional plastic strain. Three types of fatigue crack initiation were observed: long crystallographic Stage I surface initiation, internal crystallographic initiation related to structural defects and initiation on defect followed by Stage II crack propagation.
- High-cycle fatigue/creep behaviour of cast nickel base superalloy IN713LC was experimentally examined at 800 C in air. Experiments were aimed on determination of cyclic creep rate, time to fracture, kind and mode of damage. An attempt has been made to explain the cyclic creep behaviour by a balance between an effect of decrease of plastic strain response with increasing strain rate in a loading cycle and an accelerating effect of the cyclic plasticity on the development of unidirectional plastic strain. Three types of fatigue crack initiation were observed: long crystallographic Stage I surface initiation, internal crystallographic initiation related to structural defects and initiation on defect followed by Stage II crack propagation. (en)
- Práca predstavuje experimentálne výsledky charakterizujúce interakciu vysokocyklovej únavy a creepu u liatej Ni-superzliatine IN713LC. Príspevok vysvetľuje vplyv ťahového stredného napatia a superponácie amplitúdy napatia na stredné napatie na životnosť a sposob porušenia daného materiálu. (cs)
|
Title
| - High temperature high cycle fatigue behavior of Ni base superalloy IN 713 LC at tensile mean stress
- High temperature high cycle fatigue behavior of Ni base superalloy IN 713 LC at tensile mean stress (en)
- Vysokoteplotné vysokocyklové správanie Ni-superzliatiny IN713LC pri ťahovom strednom napatí (cs)
|
skos:prefLabel
| - High temperature high cycle fatigue behavior of Ni base superalloy IN 713 LC at tensile mean stress
- High temperature high cycle fatigue behavior of Ni base superalloy IN 713 LC at tensile mean stress (en)
- Vysokoteplotné vysokocyklové správanie Ni-superzliatiny IN713LC pri ťahovom strednom napatí (cs)
|
skos:notation
| - RIV/00216305:26210/06:PU65355!RIV07-MSM-26210___
|
http://linked.open.../vavai/riv/strany
| |
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/00216305:26210/06:PU65355
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - IN713LC, creep-fatigue interaction, mean stress (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| - Ústav fyziky materiálů AVČR, Žižkova 22, B
|
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| - Víceúrovňový design pokrokových materiálů
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| |
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| - Akademie věd České republiky
|
https://schema.org/isbn
| |
http://localhost/t...ganizacniJednotka
| |