About: Roughness analysis of local fatigue fracture surface Goto Sponge Distinct Permalink

An Entity of Type : http://linked.opendata.cz/ontology/domain/vavai/Vysledek, within Data Space : linked.opendata.cz associated with source document(s)

Attributes	Values
rdf:type	skos:Concept http://linked.opendata.cz/ontology/domain/vavai/Vysledek
Description	A stereophotogrammetrical analysis in scan electron microscopy is used to investigate the fracture morphology of the high-strength low-alloy steel generated under combined bendingtorsion fatigue loading. The fatigue life of investigated specimens was in the order of 106 cycles (high cycle fatigue). Roughness characteristics studied in two mutually perpendicular directions on facets in the region of crack initiation were found to be sensitive to the crack front positron. The investigation of surface topography revealed the presence of the opening Mode I in all investigated crack front locations. A stereophotogrammetrical analysis in scan electron microscopy is used to investigate the fracture morphology of the high-strength low-alloy steel generated under combined bendingtorsion fatigue loading. The fatigue life of investigated specimens was in the order of 106 cycles (high cycle fatigue). Roughness characteristics studied in two mutually perpendicular directions on facets in the region of crack initiation were found to be sensitive to the crack front positron. The investigation of surface topography revealed the presence of the opening Mode I in all investigated crack front locations. (en)
Title	Roughness analysis of local fatigue fracture surface Roughness analysis of local fatigue fracture surface (en)
skos:prefLabel	Roughness analysis of local fatigue fracture surface Roughness analysis of local fatigue fracture surface (en)
skos:notation	RIV/68378297:_____/13:00395946!RIV14-AV0-68378297
http://linked.open...avai/predkladatel	Ústav teoretické a aplikované mechaniky AV ČR, v. v. i.
http://linked.open...avai/riv/aktivita	I S
http://linked.open...avai/riv/aktivity	I, S
http://linked.open...iv/cisloPeriodika	2
http://linked.open...vai/riv/dodaniDat	2014
http://linked.open...aciTvurceVysledku	Major, Štěpán
http://linked.open.../riv/druhVysledku	J - Článek v odborném periodiku
http://linked.open...iv/duvernostUdaju	S - Úplné a pravdivé údaje nepodléhající ochraně podle zvláštních právních předpisů
http://linked.open...titaPredkladatele	Ústav teoretické a aplikované mechaniky AV ČR, v. v. i.
http://linked.open...dnocenehoVysledku	103510
http://linked.open...ai/riv/idVysledku	RIV/68378297:_____/13:00395946
http://linked.open...riv/jazykVysledku	eng - angličtina
http://linked.open.../riv/klicovaSlova	bending-torsion; biaxial loading; fatigue; fractography (en)
http://linked.open.../riv/klicoveSlovo	fractography biaxial loading fatigue bending-torsion
http://linked.open...odStatuVydavatele	US - Spojené státy americké
http://linked.open...ontrolniKodProRIV	[B5640EE683F1]
http://linked.open...i/riv/nazevZdroje	International Journal of Mechanics
http://linked.open...in/vavai/riv/obor	JJ
http://linked.open...ichTvurcuVysledku	1 (xsd:int)
http://linked.open...cetTvurcuVysledku	2 (xsd:int)
http://linked.open...UplatneniVysledku	2013
http://linked.open...v/svazekPeriodika	7
http://linked.open...iv/tvurceVysledku	Major, Štěpán Hubálovský, Š.
issn	1998-4448
number of pages	8 (xsd:int)

Faceted Search & Find service v1.16.118 as of Jun 21 2024

Alternative Linked Data Documents: ODE Content Formats:

RDF

ODATA

Microdata

About

OpenLink Virtuoso version 07.20.3240 as of Jun 21 2024, on Linux (x86_64-pc-linux-gnu), Single-Server Edition (126 GB total memory, 91 GB memory in use)
Data on this page belongs to its respective rights holders.
Virtuoso Faceted Browser Copyright © 2009-2024 OpenLink Software