| - A dynamic study of the thermal decomposition of FeC2O42H2O has been carried out in air in the range of 25-500 °C with a heating rate of 5 oC/min using the conventional methods of thermal analysis including TG and DSC. The phase composition at different calcination temperatures was determined from 57Fe Mössbauer spectra. It was found that the primary dehydration and liberation of carbon oxides from the oxalate structure is followed by a direct oxidation of Fe(II) to nanocrystalline Fe2O3 with a large surface area of about 250 m2/g. Such nanopowder is comprised of nanocrystalline particles of - and -Fe2O3 as proved by XRD, low temperature Mössbauer spectroscopy and HRTEM analysis. In contradiction with the literature assumption, no traces of magnetite (Fe3O4) have been identified during the oxidative decomposition in air. The simultaneous formation of both - and -Fe2O3 polymorphs at low temperatures is followed by an isochemical structural chan
- A dynamic study of the thermal decomposition of FeC2O42H2O has been carried out in air in the range of 25-500 °C with a heating rate of 5 oC/min using the conventional methods of thermal analysis including TG and DSC. The phase composition at different calcination temperatures was determined from 57Fe Mössbauer spectra. It was found that the primary dehydration and liberation of carbon oxides from the oxalate structure is followed by a direct oxidation of Fe(II) to nanocrystalline Fe2O3 with a large surface area of about 250 m2/g. Such nanopowder is comprised of nanocrystalline particles of - and -Fe2O3 as proved by XRD, low temperature Mössbauer spectroscopy and HRTEM analysis. In contradiction with the literature assumption, no traces of magnetite (Fe3O4) have been identified during the oxidative decomposition in air. The simultaneous formation of both - and -Fe2O3 polymorphs at low temperatures is followed by an isochemical structural chan (en)
- Tepelný rozklad dihydrátu šťavelanu železnatého v dynamických teplotních podmínkách byl studován na vzduchu v rozsahu teplot 25-500 °C s nárůstem 5 °C/min užitím termogravimetrické analýzy a diferenční skenovací kalorimetrie. Fázové složení vzorků kalcinovaných při různých teplotách bylo určováno na základě 57Fe Mössbauerových spekter. Bylo zjištěno, že po primární dehydrataci a uvolnění oxidů uhlíku ze struktury šťavelanu následuje přímá oxidace Fe(II) na nanokrystalický Fe2O3 s velkou plochou povrchu asi 250 m2/g. Takový nanoprášek je složen z nanokrystalických částic gama- a alfa-Fe2O3 v souladu s výsledky rentgenové práškové difrakce, nízkoteplotní Mössbauerovy spektroskopie a TEM analýzy s vysokým rozlišením. V rozporu s literárními údaji nebyly identifikovány ani stopy magnetitu (Fe3O4) během oxidativního rozkladu na vzduchu. Současná tvorba gama- a alfa-Fe2O3 polymorfů při nízkých teplotách je následována isochemickou strukturní transformací maghemitu na hematit. Porovnání Mössbauerových spekte (cs)
|
| Title
| - Nanocrystalline Iron(III) Oxides Formed under Dynamic Heathing of Ferrous Oxalate Dihydrate in Air
- Nanocrystalline Iron(III) Oxides Formed under Dynamic Heathing of Ferrous Oxalate Dihydrate in Air (en)
- Nanokrystalické fáze ixidu železitého připravené tepelným rozkladem dihydrátu šťavelanu železnatého na vzduchu (cs)
|
| skos:prefLabel
| - Nanocrystalline Iron(III) Oxides Formed under Dynamic Heathing of Ferrous Oxalate Dihydrate in Air
- Nanocrystalline Iron(III) Oxides Formed under Dynamic Heathing of Ferrous Oxalate Dihydrate in Air (en)
- Nanokrystalické fáze ixidu železitého připravené tepelným rozkladem dihydrátu šťavelanu železnatého na vzduchu (cs)
|
| skos:notation
| - RIV/61989592:15310/05:00001901!RIV06-GA0-15310___
|
| http://linked.open.../vavai/riv/strany
| |
| http://linked.open...avai/riv/aktivita
| |
| http://linked.open...avai/riv/aktivity
| |
| http://linked.open...iv/cisloPeriodika
| |
| http://linked.open...vai/riv/dodaniDat
| |
| http://linked.open...aciTvurceVysledku
| |
| http://linked.open.../riv/druhVysledku
| |
| http://linked.open...iv/duvernostUdaju
| |
| http://linked.open...titaPredkladatele
| |
| http://linked.open...dnocenehoVysledku
| |
| http://linked.open...ai/riv/idVysledku
| - RIV/61989592:15310/05:00001901
|
| http://linked.open...riv/jazykVysledku
| |
| http://linked.open.../riv/klicovaSlova
| - Nanocrystalline Iron(III) Oxides (en)
|
| http://linked.open.../riv/klicoveSlovo
| |
| http://linked.open...odStatuVydavatele
| - US - Spojené státy americké
|
| http://linked.open...ontrolniKodProRIV
| |
| http://linked.open...i/riv/nazevZdroje
| - AIP Conference Proceedings
|
| http://linked.open...in/vavai/riv/obor
| |
| http://linked.open...ichTvurcuVysledku
| |
| http://linked.open...cetTvurcuVysledku
| |
| http://linked.open...vavai/riv/projekt
| |
| http://linked.open...UplatneniVysledku
| |
| http://linked.open...v/svazekPeriodika
| |
| http://linked.open...iv/tvurceVysledku
| - Heřmánek, Martin
- Zbořil, Radek
- Mašláň, Miroslav
- Machala, Libor
|
| issn
| |
| number of pages
| |
| http://localhost/t...ganizacniJednotka
| |
| is http://linked.open...avai/riv/vysledek
of | |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)