| - MoSeC vrstvy byly připraveny metodou magnetronového naprašování z uhlíkového targetu, na kterém byly v erozní zóně položeny pelety MoSe2. Vrstvy vykázaly tvrdost do 5GPa, která rostla se zvyšujícím se obsahem uhlíku z 29 do 70 at.%. (cs)
- The Mo-Se-C coatings were prepared by r.f. magnetron sputtering from pure carbon target with MoSe2 pellets placed in the erosion zone, while the second target, titanium, was used to deposit a thin interlayer improving coating-substrate adhesion. The chemical composition measured by electron probe microanalysis varied from 29 to 70 at.% of carbon as a function of number of pellets; the Se/Mo ratio was close to 2 and oxygen content decreased with carbon from 5 to 2 at.%. The coatings exhibited hardness increasing with carbon content reaching a maximum value of 5 GPa.
- The Mo-Se-C coatings were prepared by r.f. magnetron sputtering from pure carbon target with MoSe2 pellets placed in the erosion zone, while the second target, titanium, was used to deposit a thin interlayer improving coating-substrate adhesion. The chemical composition measured by electron probe microanalysis varied from 29 to 70 at.% of carbon as a function of number of pellets; the Se/Mo ratio was close to 2 and oxygen content decreased with carbon from 5 to 2 at.%. The coatings exhibited hardness increasing with carbon content reaching a maximum value of 5 GPa. (en)
|
Title
| - Tribological analysis of MoSeC coatings: from nano to macroscale
- Tribologická analýza MoSeC vrstev - od nano po makroměřítko (cs)
- Tribological analysis of MoSeC coatings: from nano to macroscale (en)
|
skos:prefLabel
| - Tribological analysis of MoSeC coatings: from nano to macroscale
- Tribologická analýza MoSeC vrstev - od nano po makroměřítko (cs)
- Tribological analysis of MoSeC coatings: from nano to macroscale (en)
|
skos:notation
| - RIV/68407700:21230/08:06145600!RIV09-GA0-21230___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/68407700:21230/08:06145600
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - self-lubricant coatings (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...v/mistoKonaniAkce
| |
http://linked.open...i/riv/mistoVydani
| |
http://linked.open...i/riv/nazevZdroje
| - Proceedings of the SAIT International Tribology Conference Tribology 2008
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...iv/tvurceVysledku
| - Cavaleiro, A.
- Evaristo, M.
- Polcar, Tomáš
- Colaco, R.
|
http://linked.open...vavai/riv/typAkce
| |
http://linked.open.../riv/zahajeniAkce
| |
number of pages
| |
http://purl.org/ne...btex#hasPublisher
| |
https://schema.org/isbn
| |
http://localhost/t...ganizacniJednotka
| |