| - Rare-earth(RE = Ce, Pr, Sm, Eu, Tb)doped ternary sulfides having the general formula RbLa0.99RE0.01S2 and undoped RbLaS2 were synthesized. X-ray powder diffraction confirmed the single crystalline phase of the rhombohedral lattice system (space group R-3 m, α-NaFeO2 structure type) with hexagonality c/a = 5.34, consistent with the already reported RbLaS2 structure. Time-resolved luminescence spectroscopy was employed to investigate radioluminescence, photoluminescence, decay kinetics and absorption spectra. An RbLaS2 band edge at 322 nm was found and characteristic Pr3+, Sm3+ and Tb3+ 4f–4f emission lines in the visible spectral range were observed. The charge transfer transitions in the Pr3+- and Sm3+-related excitation spectra in the range 330–350 nm are described and the efficient energy transfer from the host to the emission centers is revealed. We discuss the potential for application in field emission displays, white LED solid-state lighting and X-ray phosphors.
- Rare-earth(RE = Ce, Pr, Sm, Eu, Tb)doped ternary sulfides having the general formula RbLa0.99RE0.01S2 and undoped RbLaS2 were synthesized. X-ray powder diffraction confirmed the single crystalline phase of the rhombohedral lattice system (space group R-3 m, α-NaFeO2 structure type) with hexagonality c/a = 5.34, consistent with the already reported RbLaS2 structure. Time-resolved luminescence spectroscopy was employed to investigate radioluminescence, photoluminescence, decay kinetics and absorption spectra. An RbLaS2 band edge at 322 nm was found and characteristic Pr3+, Sm3+ and Tb3+ 4f–4f emission lines in the visible spectral range were observed. The charge transfer transitions in the Pr3+- and Sm3+-related excitation spectra in the range 330–350 nm are described and the efficient energy transfer from the host to the emission centers is revealed. We discuss the potential for application in field emission displays, white LED solid-state lighting and X-ray phosphors. (en)
|
Title
| - Preparation, luminescence and structural properties of RE-doped RbLaS2 compounds
- Preparation, luminescence and structural properties of RE-doped RbLaS2 compounds (en)
|
skos:prefLabel
| - Preparation, luminescence and structural properties of RE-doped RbLaS2 compounds
- Preparation, luminescence and structural properties of RE-doped RbLaS2 compounds (en)
|
skos:notation
| - RIV/68378271:_____/11:00374678!RIV12-AV0-68378271
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| - P(KAN300100802), P(TA01011017), Z(AV0Z10100520), Z(AV0Z10100521)
|
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/68378271:_____/11:00374678
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - X-ray diffraction; optical materials; crystal growth; luminescence (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| - GB - Spojené království Velké Británie a Severního Irska
|
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| |
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...vavai/riv/projekt
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Boháček, Pavel
- Nikl, Martin
- Jarý, Vítězslav
- Bárta, J.
- Havlák, Lubomír
|
http://linked.open...ain/vavai/riv/wos
| |
http://linked.open...n/vavai/riv/zamer
| |
issn
| |
number of pages
| |
http://bibframe.org/vocab/doi
| - 10.1016/j.actamat.2011.06.019
|