| - The paper deals with the mechanism of eutectic formation in a nickel coated aluminium system after heat treatment. The initial coating was produced from a nickel powder by means of high velocity oxyfuel (HVOF) spraying onto an aluminium sheet substrate. Specimens for investigations were manufactured immediately after the spraying. The specimens were heat-treated using a differential thermal analysis (DTA) apparatus up to the temperature of 700 or 900 degrees C and then cooled down to room temperature in argon atmosphere with a constant heating and cooling rate of 5 degrees C / min, under which Al-Al3Ni + Al3Ni hypereutectic alloys were formed within the initial substrate. Two different alloy microstructures consisting of intermetallic layers and coarse eutectic or an ultrafine well-dispersed eutectic were formed. Formation processes and resulting microstructures were studied by means of DTA, metallography, scanning electron microscopy, focused ion beam, energy dispersive microanalysis and image analysis techniques.
- The paper deals with the mechanism of eutectic formation in a nickel coated aluminium system after heat treatment. The initial coating was produced from a nickel powder by means of high velocity oxyfuel (HVOF) spraying onto an aluminium sheet substrate. Specimens for investigations were manufactured immediately after the spraying. The specimens were heat-treated using a differential thermal analysis (DTA) apparatus up to the temperature of 700 or 900 degrees C and then cooled down to room temperature in argon atmosphere with a constant heating and cooling rate of 5 degrees C / min, under which Al-Al3Ni + Al3Ni hypereutectic alloys were formed within the initial substrate. Two different alloy microstructures consisting of intermetallic layers and coarse eutectic or an ultrafine well-dispersed eutectic were formed. Formation processes and resulting microstructures were studied by means of DTA, metallography, scanning electron microscopy, focused ion beam, energy dispersive microanalysis and image analysis techniques. (en)
|
Title
| - Effect of heat treatment on formation of Al-Al3Ni hypereutectic alloys
- Effect of heat treatment on formation of Al-Al3Ni hypereutectic alloys (en)
|
skos:prefLabel
| - Effect of heat treatment on formation of Al-Al3Ni hypereutectic alloys
- Effect of heat treatment on formation of Al-Al3Ni hypereutectic alloys (en)
|
skos:notation
| - RIV/61989100:27360/14:86092411!RIV15-MSM-27360___
|
http://linked.open...avai/riv/aktivita
| |
http://linked.open...avai/riv/aktivity
| |
http://linked.open...iv/cisloPeriodika
| |
http://linked.open...vai/riv/dodaniDat
| |
http://linked.open...aciTvurceVysledku
| |
http://linked.open.../riv/druhVysledku
| |
http://linked.open...iv/duvernostUdaju
| |
http://linked.open...titaPredkladatele
| |
http://linked.open...dnocenehoVysledku
| |
http://linked.open...ai/riv/idVysledku
| - RIV/61989100:27360/14:86092411
|
http://linked.open...riv/jazykVysledku
| |
http://linked.open.../riv/klicovaSlova
| - microscopy; differential thermal analysis; thermal spraying; aluminides; Aluminium (en)
|
http://linked.open.../riv/klicoveSlovo
| |
http://linked.open...odStatuVydavatele
| - CH - Švýcarská konfederace
|
http://linked.open...ontrolniKodProRIV
| |
http://linked.open...i/riv/nazevZdroje
| - Key Engineering Materials
|
http://linked.open...in/vavai/riv/obor
| |
http://linked.open...ichTvurcuVysledku
| |
http://linked.open...cetTvurcuVysledku
| |
http://linked.open...UplatneniVysledku
| |
http://linked.open...v/svazekPeriodika
| |
http://linked.open...iv/tvurceVysledku
| - Klakurková, Lenka
- Slámečka, Karel
- Smetana, Bedřich
- Čelko, Ladislav
- Švejcar, Jiří
- Žaludová, Monika
- Grzonka, Justyna
- Lewandowska, Malgorzata
- Plocinski, Tomasz
|
http://linked.open...ain/vavai/riv/wos
| |
issn
| |
number of pages
| |
http://bibframe.org/vocab/doi
| - 10.4028/www.scientific.net/KEM.592-593.513
|
http://localhost/t...ganizacniJednotka
| |